Dental gold alloys with age-hardenability at intraoral temperature

M. Ohta, T. Shiraishi, Masaharu Nakagawa, S. Matsuya

研究成果: Contribution to journalArticle査読

21 被引用数 (Scopus)

抄録

Dental gold alloys with age-hardenability at intraoral temperature were developed. Either 3 or 6 at% Ga, Al, Zn, In, Ni or Pd were added to an equiatomic AuCu alloy and the effect of additives on the low-temperature age-hardenability was examined. Alloys containing Ga, Al or Zn exhibited excellent low-temperature age-hardenability. The hardness of an alloy containing 6 at% Ga or 6 at% Al was doubled in one to ten days by ageing at 37 °C. Pronounced hardening was not demonstrated in an as-cast alloy, but solution treatment for only a few minutes provided enough age-hardenability. The age-hardening rate at low temperature related closely with the melting temperature of the alloy. Experimental gold alloys exhibited electrochemical behaviour similar to that of a commercial Type IV gold alloy. It is therefore concluded that AuCu alloy with added Ga, Al or Zn is expected to have enough age-hardenability and corrosion resistance for clinical use in the oral environment.

本文言語英語
ページ(範囲)2083-2086
ページ数4
ジャーナルJournal of Materials Science
29
8
DOI
出版ステータス出版済み - 4 1 1994

All Science Journal Classification (ASJC) codes

  • 凝縮系物理学
  • 電子材料、光学材料、および磁性材料
  • 材料科学(全般)

フィンガープリント

「Dental gold alloys with age-hardenability at intraoral temperature」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル