Dependence of crystal structure, phase transition temperature, chemical state of Fe, oxygen content and electrical conductivity of Ba2-xLaxFe2O5 + δ (x = 0.00-0.15) on la content

Tsubasa Sato, Takashi Okiba, Katsumi Shozugawa, Motoyuki Matsuo, Fumito Fujishiro, Eiki Niwa, Takuya Hashimoto

研究成果: Contribution to journalArticle査読

8 被引用数 (Scopus)

抄録

Single phase preparation, crystal structure and structure phase transition by temperature of Ba2-xLaxFe2O5 + δ (x = 0.00-0.15), which is regarded to be promising as high electrical conduction material at high temperature, were investigated. Single phase with monoclinic structure at room temperature could be successfully prepared employing sintering under N2 atmosphere with 10- 4 bar of oxygen partial pressure. Abrupt increase of molar volume and discrete decrease of temperature for the structural phase transition from monoclinic to cubic between x = 0.05 and x = 0.10 indicated existence of phase transition by La content. From iodometric titration, it was revealed that the specimens with x less than 0.05 were oxygen deficient while those with x more than 0.10 were oxygen excess from stoichiometric composition of 5.00. By combining Mössbauer spectra and iodometric titration, it was concluded that Ba2Fe2O5 + δ contained both Fe3 + and Fe2 +. Concentration of Fe2 + decreased with increasing La content from 0.00 to 0.05. Fe2 + disappeared for the specimens with x larger than 0.10, showing correspondence with the phase transition by La content. For the specimens with x less than 0.05, discrete increase originating from structural phase transition from monoclinic to cubic was observed in temperature dependence of electrical conductivity. For the specimen with x = 0.10, even monoclinic phase showed high electrical conductivity comparable to ones of cubic, which could be originating from the phase transition by La content from oxygen deficient phase to oxygen excess one. Not discrete but continuous variation owing to the structural phase transition from monoclinic to cubic was observed in temperature dependence of electrical conductivity of the specimen with x = 0.10.

本文言語英語
ページ(範囲)71-76
ページ数6
ジャーナルSolid State Ionics
290
DOI
出版ステータス出版済み - 7 1 2016
外部発表はい

All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Dependence of crystal structure, phase transition temperature, chemical state of Fe, oxygen content and electrical conductivity of Ba<sub>2-x</sub>La<sub>x</sub>Fe<sub>2</sub>O<sub>5 + δ</sub> (x = 0.00-0.15) on la content」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル