Deterioration progress and performance reduction of 40-year-old reinforced concrete beams in natural corrosion environments

Amry Dasar, Hidenori Hamada, Yasutaka Sagawa, Daisuke Yamamoto

研究成果: ジャーナルへの寄稿記事

11 引用 (Scopus)

抄録

Deterioration progress and performance reduction were experimentally evaluated in 40-year-old corroded reinforced concrete (RC) beams. The corrosion process was natural, without acceleration by current application, admixture inclusion, or exposure to an artificial chloride environment. The mechanical performance of the beams was evaluated through a four-point bending test. The corroded steel reinforcing bars were extracted for corrosion evaluation and tensile testing. A good correlation was established between crack width and cross-section loss, as well as between cross-section loss and ultimate capacity loss. Furthermore, the relationship between deterioration progress and performance degradation with the exposure period for each deterioration stage was elucidated.

元の言語英語
ページ(範囲)690-704
ページ数15
ジャーナルConstruction and Building Materials
149
DOI
出版物ステータス出版済み - 9 15 2017

Fingerprint

Deterioration
Reinforced concrete
Corrosion
Steel
Tensile testing
Bending tests
Chlorides
Cracks
Degradation

All Science Journal Classification (ASJC) codes

  • Civil and Structural Engineering
  • Building and Construction
  • Materials Science(all)

これを引用

@article{b59c05bd96a34da6999175d112d37736,
title = "Deterioration progress and performance reduction of 40-year-old reinforced concrete beams in natural corrosion environments",
abstract = "Deterioration progress and performance reduction were experimentally evaluated in 40-year-old corroded reinforced concrete (RC) beams. The corrosion process was natural, without acceleration by current application, admixture inclusion, or exposure to an artificial chloride environment. The mechanical performance of the beams was evaluated through a four-point bending test. The corroded steel reinforcing bars were extracted for corrosion evaluation and tensile testing. A good correlation was established between crack width and cross-section loss, as well as between cross-section loss and ultimate capacity loss. Furthermore, the relationship between deterioration progress and performance degradation with the exposure period for each deterioration stage was elucidated.",
author = "Amry Dasar and Hidenori Hamada and Yasutaka Sagawa and Daisuke Yamamoto",
year = "2017",
month = "9",
day = "15",
doi = "10.1016/j.conbuildmat.2017.05.162",
language = "English",
volume = "149",
pages = "690--704",
journal = "Construction and Building Materials",
issn = "0950-0618",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Deterioration progress and performance reduction of 40-year-old reinforced concrete beams in natural corrosion environments

AU - Dasar, Amry

AU - Hamada, Hidenori

AU - Sagawa, Yasutaka

AU - Yamamoto, Daisuke

PY - 2017/9/15

Y1 - 2017/9/15

N2 - Deterioration progress and performance reduction were experimentally evaluated in 40-year-old corroded reinforced concrete (RC) beams. The corrosion process was natural, without acceleration by current application, admixture inclusion, or exposure to an artificial chloride environment. The mechanical performance of the beams was evaluated through a four-point bending test. The corroded steel reinforcing bars were extracted for corrosion evaluation and tensile testing. A good correlation was established between crack width and cross-section loss, as well as between cross-section loss and ultimate capacity loss. Furthermore, the relationship between deterioration progress and performance degradation with the exposure period for each deterioration stage was elucidated.

AB - Deterioration progress and performance reduction were experimentally evaluated in 40-year-old corroded reinforced concrete (RC) beams. The corrosion process was natural, without acceleration by current application, admixture inclusion, or exposure to an artificial chloride environment. The mechanical performance of the beams was evaluated through a four-point bending test. The corroded steel reinforcing bars were extracted for corrosion evaluation and tensile testing. A good correlation was established between crack width and cross-section loss, as well as between cross-section loss and ultimate capacity loss. Furthermore, the relationship between deterioration progress and performance degradation with the exposure period for each deterioration stage was elucidated.

UR - http://www.scopus.com/inward/record.url?scp=85019971808&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85019971808&partnerID=8YFLogxK

U2 - 10.1016/j.conbuildmat.2017.05.162

DO - 10.1016/j.conbuildmat.2017.05.162

M3 - Article

VL - 149

SP - 690

EP - 704

JO - Construction and Building Materials

JF - Construction and Building Materials

SN - 0950-0618

ER -