Deuterium/tritium behavior in Flibe and Flibe-facing materials

R. A. Anderl, S. Fukada, G. R. Smolik, R. J. Pawelko, S. T. Schuetz, J. P. Sharpe, B. J. Merrill, D. A. Petti, H. Nishimura, T. Terai, S. Tanaka

研究成果: ジャーナルへの寄稿会議記事査読

32 被引用数 (Scopus)

抄録

Experimental studies to investigate the behavior of deuterium and tritium in the molten salt Flibe (2LiF·BeF2), have been conducted as part of the Japan-US joint research program (JUPITER-II). Measurements of deuterium transport were made in a cylindrically symmetric, dual permeation probe assembly containing 400 cc of Flibe. An exact analytical transport solution in cylindrical coordinates was fit to the measured permeation data, and this analysis derived deuterium diffusion and solubility coefficients of 8.0×10-10 m2/s and 3.1×10-4 mol/m3Pa at 600 °C, respectively, and 3.0×10-9 m2/s and 1.0×10-4 mol/m3Pa at 650 °C. The diffusion coefficients were about a factor of two less than previous results derived from capillary-reservoir diffusion measurements with tritium. Solubility results were significantly greater than previously measured for D2 but they were comparable to those for DF in Flibe. The results suggest that the dominant deuterium transport species in Flibe was D +F- for these experiments.

本文言語英語
ページ(範囲)1327-1331
ページ数5
ジャーナルJournal of Nuclear Materials
329-333
1-3 PART B
DOI
出版ステータス出版済み - 8月 1 2004
イベントProceedings of the 11th Conference on Fusion Research - Kyoto, 日本
継続期間: 12月 7 200312月 12 2003

!!!All Science Journal Classification (ASJC) codes

  • 核物理学および高エネルギー物理学
  • 材料科学(全般)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「Deuterium/tritium behavior in Flibe and Flibe-facing materials」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル