Development of Cu substrate for low cost coated conductors

Naoji Kashima, Kunihiro Shima, Toshiya Doi, Shuichi Kubota, Tomonori Watanabe, Masayoshi Inoue, Tananobu Kiss, Shigeo Nagaya

研究成果: Contribution to journalArticle査読

9 被引用数 (Scopus)

抄録

A textured Cu {100} (001) substrate for practical use in low cost coated conductor applications has been successfully fabricated. A textured Cu substrate is a promising substrate for a coated conductor template. This is the result of a low material cost base, no magnetization loss and good electro conductivity. One of the issues for a Cu substrate is surface oxidation. During REBCO deposition, the Cu substrate is exposed to an oxygen atmosphere, and de-lamination of the buffer layer can occur. To prevent this issue a thin Ni layer was formed on the textured Cu substrate by electroplating. After a further annealing process the Ni electroplated Cu substrates exhibit a good sharp texture and a smoother surface. The Δφ and Δ of the substrate were about 4.6 and 4.5 degrees, respectively. The surface roughness was estimated at 6.8 nm Ra by AFM. Using this substrate and clad type Cu/SUS316 substrates, we deposited a CeO2/YSZ/CeO2 layer by Pulsed Laser Deposition (PLD) and an YBa2Cu3O7-δ layer by PLD and Metal-Organic Chemical Vapor Deposition (MOCVD). The results show no occurrence of de-lamination. Typical critical temperature of the coated conductors was 90.5 K and critical current density was a maximum of 4.5 MA/cm2 (at 77 K in a self-field).

本文言語英語
論文番号5153249
ページ(範囲)3299-3302
ページ数4
ジャーナルIEEE Transactions on Applied Superconductivity
19
3
DOI
出版ステータス出版済み - 6 2009

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

フィンガープリント 「Development of Cu substrate for low cost coated conductors」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル