Development of Tri-axial superconducting cable system for type test

Tasuku Kitamura, Kazuhisa Adachi, Hideo Sugane, Tatsuhisa Nakanishi, Yuji Aoki, Nobuhiro Mido, Masataka Iwakuma, Takayo Hasegawa

研究成果: ジャーナルへの寄稿Conference article

抄録

We developed a tri-axial superconducting cable system with the rated voltage of 22kV and operating current of 3 kA at liquid nitrogen temperature. We designed the superconducting cable and the termination that was cooled subcooled liquid nitrogen. We used in-house YBCO tapes and a winding machine to prepare the conductor that the I c-value of 4,200 A or more per phase at liquid nitrogen temperature. The outer diameters of the conductor and the cryostat were approximately 50 mm and 130 mm, respectively. The length, the diameter and weight of each termination were approximately 4,000 mm, 450 mm and 600 kg. The thickness of the insulation layer, which was made from made from PPL paper, was determined by estimation of minimum break down electrical field from Weibull distribution analysis of results, which were obtained by break down tests of the model cables. Regarding the cooling condition of the cooling system, the liquid nitrogen temperatures of the inlet and the outlet of cable system was designed to be 65 K and 70 K, respectively. We manufactured a 25 m tri-axial superconducting cable, and cut out it to get 2 m samples for the I c test and voltage test at liquid nitrogen temperature. The critical current of each phase was higher than 4,500 A. There was no break-down of each insulation phase at 52 kV for 30 minutes the voltage test. We also manufactured a pair of termination connection for system test and no break-down occurred each insulation phase at 52 kV for 30 minutes. We performed type test of cable system including the superconducting cable and the termination, based on "Recommendations for Testing of Superconducting cables (CIGRE Technical Brochures 538)" [1].

元の言語英語
記事番号012075
ジャーナルJournal of Physics: Conference Series
1054
発行部数1
DOI
出版物ステータス出版済み - 7 26 2018
イベント30th International Symposium on Superconductivity, ISS 2017 - Tokyo, 日本
継続期間: 12 13 201712 15 2017

Fingerprint

cables
liquid nitrogen
breakdown
insulation
electric potential
conductors
temperature
cooling systems
cryostats
outlets
recommendations
tapes
critical current
cooling

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

これを引用

Kitamura, T., Adachi, K., Sugane, H., Nakanishi, T., Aoki, Y., Mido, N., ... Hasegawa, T. (2018). Development of Tri-axial superconducting cable system for type test. Journal of Physics: Conference Series, 1054(1), [012075]. https://doi.org/10.1088/1742-6596/1054/1/012075

Development of Tri-axial superconducting cable system for type test. / Kitamura, Tasuku; Adachi, Kazuhisa; Sugane, Hideo; Nakanishi, Tatsuhisa; Aoki, Yuji; Mido, Nobuhiro; Iwakuma, Masataka; Hasegawa, Takayo.

:: Journal of Physics: Conference Series, 巻 1054, 番号 1, 012075, 26.07.2018.

研究成果: ジャーナルへの寄稿Conference article

Kitamura, T, Adachi, K, Sugane, H, Nakanishi, T, Aoki, Y, Mido, N, Iwakuma, M & Hasegawa, T 2018, 'Development of Tri-axial superconducting cable system for type test', Journal of Physics: Conference Series, 巻. 1054, 番号 1, 012075. https://doi.org/10.1088/1742-6596/1054/1/012075
Kitamura T, Adachi K, Sugane H, Nakanishi T, Aoki Y, Mido N その他. Development of Tri-axial superconducting cable system for type test. Journal of Physics: Conference Series. 2018 7 26;1054(1). 012075. https://doi.org/10.1088/1742-6596/1054/1/012075
Kitamura, Tasuku ; Adachi, Kazuhisa ; Sugane, Hideo ; Nakanishi, Tatsuhisa ; Aoki, Yuji ; Mido, Nobuhiro ; Iwakuma, Masataka ; Hasegawa, Takayo. / Development of Tri-axial superconducting cable system for type test. :: Journal of Physics: Conference Series. 2018 ; 巻 1054, 番号 1.
@article{335334db191b47e299d384dc67b5e37b,
title = "Development of Tri-axial superconducting cable system for type test",
abstract = "We developed a tri-axial superconducting cable system with the rated voltage of 22kV and operating current of 3 kA at liquid nitrogen temperature. We designed the superconducting cable and the termination that was cooled subcooled liquid nitrogen. We used in-house YBCO tapes and a winding machine to prepare the conductor that the I c-value of 4,200 A or more per phase at liquid nitrogen temperature. The outer diameters of the conductor and the cryostat were approximately 50 mm and 130 mm, respectively. The length, the diameter and weight of each termination were approximately 4,000 mm, 450 mm and 600 kg. The thickness of the insulation layer, which was made from made from PPL paper, was determined by estimation of minimum break down electrical field from Weibull distribution analysis of results, which were obtained by break down tests of the model cables. Regarding the cooling condition of the cooling system, the liquid nitrogen temperatures of the inlet and the outlet of cable system was designed to be 65 K and 70 K, respectively. We manufactured a 25 m tri-axial superconducting cable, and cut out it to get 2 m samples for the I c test and voltage test at liquid nitrogen temperature. The critical current of each phase was higher than 4,500 A. There was no break-down of each insulation phase at 52 kV for 30 minutes the voltage test. We also manufactured a pair of termination connection for system test and no break-down occurred each insulation phase at 52 kV for 30 minutes. We performed type test of cable system including the superconducting cable and the termination, based on {"}Recommendations for Testing of Superconducting cables (CIGRE Technical Brochures 538){"} [1].",
author = "Tasuku Kitamura and Kazuhisa Adachi and Hideo Sugane and Tatsuhisa Nakanishi and Yuji Aoki and Nobuhiro Mido and Masataka Iwakuma and Takayo Hasegawa",
year = "2018",
month = "7",
day = "26",
doi = "10.1088/1742-6596/1054/1/012075",
language = "English",
volume = "1054",
journal = "Journal of Physics: Conference Series",
issn = "1742-6588",
publisher = "IOP Publishing Ltd.",
number = "1",

}

TY - JOUR

T1 - Development of Tri-axial superconducting cable system for type test

AU - Kitamura, Tasuku

AU - Adachi, Kazuhisa

AU - Sugane, Hideo

AU - Nakanishi, Tatsuhisa

AU - Aoki, Yuji

AU - Mido, Nobuhiro

AU - Iwakuma, Masataka

AU - Hasegawa, Takayo

PY - 2018/7/26

Y1 - 2018/7/26

N2 - We developed a tri-axial superconducting cable system with the rated voltage of 22kV and operating current of 3 kA at liquid nitrogen temperature. We designed the superconducting cable and the termination that was cooled subcooled liquid nitrogen. We used in-house YBCO tapes and a winding machine to prepare the conductor that the I c-value of 4,200 A or more per phase at liquid nitrogen temperature. The outer diameters of the conductor and the cryostat were approximately 50 mm and 130 mm, respectively. The length, the diameter and weight of each termination were approximately 4,000 mm, 450 mm and 600 kg. The thickness of the insulation layer, which was made from made from PPL paper, was determined by estimation of minimum break down electrical field from Weibull distribution analysis of results, which were obtained by break down tests of the model cables. Regarding the cooling condition of the cooling system, the liquid nitrogen temperatures of the inlet and the outlet of cable system was designed to be 65 K and 70 K, respectively. We manufactured a 25 m tri-axial superconducting cable, and cut out it to get 2 m samples for the I c test and voltage test at liquid nitrogen temperature. The critical current of each phase was higher than 4,500 A. There was no break-down of each insulation phase at 52 kV for 30 minutes the voltage test. We also manufactured a pair of termination connection for system test and no break-down occurred each insulation phase at 52 kV for 30 minutes. We performed type test of cable system including the superconducting cable and the termination, based on "Recommendations for Testing of Superconducting cables (CIGRE Technical Brochures 538)" [1].

AB - We developed a tri-axial superconducting cable system with the rated voltage of 22kV and operating current of 3 kA at liquid nitrogen temperature. We designed the superconducting cable and the termination that was cooled subcooled liquid nitrogen. We used in-house YBCO tapes and a winding machine to prepare the conductor that the I c-value of 4,200 A or more per phase at liquid nitrogen temperature. The outer diameters of the conductor and the cryostat were approximately 50 mm and 130 mm, respectively. The length, the diameter and weight of each termination were approximately 4,000 mm, 450 mm and 600 kg. The thickness of the insulation layer, which was made from made from PPL paper, was determined by estimation of minimum break down electrical field from Weibull distribution analysis of results, which were obtained by break down tests of the model cables. Regarding the cooling condition of the cooling system, the liquid nitrogen temperatures of the inlet and the outlet of cable system was designed to be 65 K and 70 K, respectively. We manufactured a 25 m tri-axial superconducting cable, and cut out it to get 2 m samples for the I c test and voltage test at liquid nitrogen temperature. The critical current of each phase was higher than 4,500 A. There was no break-down of each insulation phase at 52 kV for 30 minutes the voltage test. We also manufactured a pair of termination connection for system test and no break-down occurred each insulation phase at 52 kV for 30 minutes. We performed type test of cable system including the superconducting cable and the termination, based on "Recommendations for Testing of Superconducting cables (CIGRE Technical Brochures 538)" [1].

UR - http://www.scopus.com/inward/record.url?scp=85051347842&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85051347842&partnerID=8YFLogxK

U2 - 10.1088/1742-6596/1054/1/012075

DO - 10.1088/1742-6596/1054/1/012075

M3 - Conference article

VL - 1054

JO - Journal of Physics: Conference Series

JF - Journal of Physics: Conference Series

SN - 1742-6588

IS - 1

M1 - 012075

ER -