Diffusion in ultrafine-grained Al-Mg alloys

T. Fujita, H. Hasegawa, Z. Horita, T. G. Langdon

    研究成果: Contribution to journalArticle査読

    14 被引用数 (Scopus)

    抄録

    Grain sizes of less than 1 μm were produced in Al-0.2%Sc (or 0.2%Zr) and Al-3%Mg-0.2%Sc (or 0.2%Zr) alloys using the technique of equal-channel angular pressing (ECAP). These alloys were coupled and they were subjected to diffusion annealing at a temperature in the range of 523 to 773 K. Interdiffusion coefficients were determined from the concentration gradients measured across the interface and a comparison was made with those of coarse-grained diffusion couples. Interdiffusion coefficients of the fine-grained couples are significantly higher than those of the coarse-grained couples at lower annealing temperatures. Grain boundary diffusion coefficients of Mg in Al were deduced from the measurements.

    本文言語英語
    ページ(範囲)1205-1210
    ページ数6
    ジャーナルDefect and Diffusion Forum
    194-199 PART 2
    DOI
    出版ステータス出版済み - 2001

    All Science Journal Classification (ASJC) codes

    • 放射線
    • 材料科学(全般)
    • 凝縮系物理学

    フィンガープリント

    「Diffusion in ultrafine-grained Al-Mg alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル