EBSP analysis of modified 9Cr-1Mo martensitic steel

Hideharu Nakashima, Daisuke Terada, Fuyuki Yoshida, Hiroyuki Hayakawa, Hiroshi Abe

研究成果: Contribution to journalArticle査読

14 被引用数 (Scopus)


In order to clarify the structure change of 9Cr-1Mo tempered martensitic steel during the high temperature creep, the structures deformed were observed by SEM-OIM and TEM method. It was found that initial block and packet structures were equi-axed. These structures were very stable during creep, but just before rupture changed to elongate grain. From an analysis of the grain boundary, ∑ 3(rotation angle 70.5°), near ∑11(rotation angle 50.5°) and small angle(rotation angle 10°) boundaries existed in the martensite. This result agrees with the result predicted with K-S orientation relationship. It was also found that the density of ∑3 boundary or near ∑11 boundary decreased during high temperature creep. But, it was found that the density of ∑3 boundary decreased, and that of near ∑11 and small angle boundaries increased during the high temperature deformation. In initial structure, relative frequency of 〈110〉 common axis(Block boundary) is largest to compare with other axes. But, just before the rupture, relative frequency of 〈110〉(Block boundary) suddenly decreased and 〈123〉 and 〈233〉(not Block or Packet boundaries) increased.

ジャーナルisij international
出版ステータス出版済み - 2001

All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学


「EBSP analysis of modified 9Cr-1Mo martensitic steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。