Effect of absorbed hydrogen on the near threshold fatigue crack growth behavior of short crack (examination on low alloy steel, carbon steel and heat resistant alloy A286)

Yoshiyuki Kondo, Masanobu Kubota, Keiko Shishime, Jun Ichiro Yamaguchi

    研究成果: Contribution to journalArticle査読

    9 被引用数 (Scopus)

    抄録

    Hydrogen is considered to be a possible energy source in the coming future. However, it has been recognized that hydrogen has a detrimental effect on the fatigue strength of metal. The fatigue crack growth characteristic is an important property for the integrity assessment of hydrogen utilization machine. In this report, the effect of absorbed hydrogen on the fatigue crack propagation characteristic in the near threshold regime was studied using low alloy steel, carbon steels and heat resistant alloy A286. Especially in this study, very short pre-cracked specimen as small as 0.03 mm deep was used. As a result, materials with Vickers hardness higher than 300 were susceptible to absorbed hydrogen irrespective of alloy system. Fatigue crack propagation was accelerated and the ΔKth was lowered about 25%. No remarkable change was observed in materials with hardness lower than 200.

    本文言語英語
    ページ(範囲)1366-1372
    ページ数7
    ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
    74
    10
    DOI
    出版ステータス出版済み - 10 2008

    All Science Journal Classification (ASJC) codes

    • 材料科学(全般)
    • 材料力学
    • 機械工学

    フィンガープリント

    「Effect of absorbed hydrogen on the near threshold fatigue crack growth behavior of short crack (examination on low alloy steel, carbon steel and heat resistant alloy A286)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル