Effect of active metal on bonding characteristics and interfacial structure of the Si3N4/Si3N4 joints brazed by Ag-Cu filler metal

Yasuhiro Morizono, Takashi Nakata, Minoru Nishida, Akira Chiba

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

Joining of Si3N4 to Si3N4 was carried out using Ag-Cu filler metal containing Ti, Zr, V and Nb as an active metal. Bonding treatment was performed at 1173 to 1473 K for 1h in a vacuum. The shear strengths of the joints brazed at 1173 to 1473 K using active filler metals containing Ti and Zr were 150 to 250 MPa. The fracture position of the joints after shear test was the filler metal or mixture of the filler metal and Si3N4. On the other hand, the average shear strengths of the joints brazed at 1373 K using active filler metals containing V and Nb were 144 and 163 MPa, respectively. The fracture position of the joints using these filler metals was the interface between filler metal and Si3N4 in all cases. The active filler metals containing Ti and Zr yielded TiN and ZrN fine grains close to the Si3N4. No fine grains were observed in the joint using active filler metal containing V and coarse columnar grains of V3Si were observed. Therefore, it is concluded that the fine grains of the nitrides formed close to the Si3N4 is responsible for the substantial bonding between filler metal and Si3N4.

本文言語英語
ページ(範囲)810-815
ページ数6
ジャーナルNippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan
103
1200
DOI
出版ステータス出版済み - 1995
外部発表はい

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

フィンガープリント 「Effect of active metal on bonding characteristics and interfacial structure of the Si<sub>3</sub>N<sub>4</sub>/Si<sub>3</sub>N<sub>4</sub> joints brazed by Ag-Cu filler metal」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル