Effect of annealing on the microstructure behavior of D+-irradiated W-2vol.%TiC composite prepared by wet-chemical method

Yu Xiang Zhang, Xiao Yue Tan, Xiang Zan, Lai Ma Luo, Yue Xu, Qiu Xu, Kazutoshi Tokunaga, Xiao Yong Zhu, Yu Cheng Wu

研究成果: Contribution to journalArticle

抜粋

W-2vol.%TiC composites were prepared through wet-chemical method combined with sintering and hot-rolling process. In this work, the evolution of damage micrograph in W-2vol.%TiC was studied by SEM in situ observation as functions of annealing temperature and implantation fluence. The results show that the surface morphology of the W matrix was slightly affected after D ions irradiation, while the dispersively distributed TiC particles were damaged severely. After annealing at 1173 K and 1573 K, the irradiation damage structure was repaired.

元の言語英語
記事番号111321
ジャーナルFusion Engineering and Design
148
DOI
出版物ステータス出版済み - 11 2019

All Science Journal Classification (ASJC) codes

  • Civil and Structural Engineering
  • Nuclear Energy and Engineering
  • Materials Science(all)
  • Mechanical Engineering

フィンガープリント Effect of annealing on the microstructure behavior of D<sup>+</sup>-irradiated W-2vol.%TiC composite prepared by wet-chemical method' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用