Effect of annealing on the pitting corrosion resistance of anodized aluminum-magnesium alloy processed by severe plastic deformation

In Joon Son, Hiroaki Nakano, Satoshi Oue, Shigeo Kobayashi, Hisaaki Fukushima, Zenji Horita

研究成果: ジャーナルへの寄稿記事

8 引用 (Scopus)

抄録

The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2mol.L-1 of AlCl3 and also by surface analysis. The degree of internal stress generated in anodic oxide films during anodization was evaluated with a strain gauge. The ECAP decreased the pitting corrosion resistance of anodized Al-Mg alloy. However, the pitting corrosion resistance was improved by annealing after the ECAP. The internal stress present in the anodic oxide films was compressive, and the stress was higher in the alloys with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion. The ECAP produces high internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasing the likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from the ECAP. The improvement in the pitting corrosion resistance of anodized Al-Mg allov by annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films.

元の言語英語
ページ(範囲)2656-2663
ページ数8
ジャーナルMaterials Transactions
49
発行部数11
DOI
出版物ステータス出版済み - 11 1 2008

Fingerprint

Equal channel angular pressing
pitting
magnesium alloys
pressing
Pitting
Magnesium alloys
corrosion resistance
aluminum alloys
plastic deformation
residual stress
Corrosion resistance
Aluminum alloys
Residual stresses
Plastic deformation
Oxide films
oxide films
Annealing
annealing
cracks
Cracks

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Effect of annealing on the pitting corrosion resistance of anodized aluminum-magnesium alloy processed by severe plastic deformation. / Son, In Joon; Nakano, Hiroaki; Oue, Satoshi; Kobayashi, Shigeo; Fukushima, Hisaaki; Horita, Zenji.

:: Materials Transactions, 巻 49, 番号 11, 01.11.2008, p. 2656-2663.

研究成果: ジャーナルへの寄稿記事

@article{9e127c49d0ee463688b7498d1b8e2bd4,
title = "Effect of annealing on the pitting corrosion resistance of anodized aluminum-magnesium alloy processed by severe plastic deformation",
abstract = "The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2mol.L-1 of AlCl3 and also by surface analysis. The degree of internal stress generated in anodic oxide films during anodization was evaluated with a strain gauge. The ECAP decreased the pitting corrosion resistance of anodized Al-Mg alloy. However, the pitting corrosion resistance was improved by annealing after the ECAP. The internal stress present in the anodic oxide films was compressive, and the stress was higher in the alloys with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion. The ECAP produces high internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasing the likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from the ECAP. The improvement in the pitting corrosion resistance of anodized Al-Mg allov by annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films.",
author = "Son, {In Joon} and Hiroaki Nakano and Satoshi Oue and Shigeo Kobayashi and Hisaaki Fukushima and Zenji Horita",
year = "2008",
month = "11",
day = "1",
doi = "10.2320/matertrans.MRA2008230",
language = "English",
volume = "49",
pages = "2656--2663",
journal = "Materials Transactions",
issn = "0916-1821",
publisher = "The Japan Institute of Metals and Materials",
number = "11",

}

TY - JOUR

T1 - Effect of annealing on the pitting corrosion resistance of anodized aluminum-magnesium alloy processed by severe plastic deformation

AU - Son, In Joon

AU - Nakano, Hiroaki

AU - Oue, Satoshi

AU - Kobayashi, Shigeo

AU - Fukushima, Hisaaki

AU - Horita, Zenji

PY - 2008/11/1

Y1 - 2008/11/1

N2 - The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2mol.L-1 of AlCl3 and also by surface analysis. The degree of internal stress generated in anodic oxide films during anodization was evaluated with a strain gauge. The ECAP decreased the pitting corrosion resistance of anodized Al-Mg alloy. However, the pitting corrosion resistance was improved by annealing after the ECAP. The internal stress present in the anodic oxide films was compressive, and the stress was higher in the alloys with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion. The ECAP produces high internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasing the likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from the ECAP. The improvement in the pitting corrosion resistance of anodized Al-Mg allov by annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films.

AB - The effect of annealing on the pitting corrosion resistance of anodized Al-Mg alloy processed by equal-channel angular pressing (ECAP) was investigated by electrochemical techniques in a solution containing 0.2mol.L-1 of AlCl3 and also by surface analysis. The degree of internal stress generated in anodic oxide films during anodization was evaluated with a strain gauge. The ECAP decreased the pitting corrosion resistance of anodized Al-Mg alloy. However, the pitting corrosion resistance was improved by annealing after the ECAP. The internal stress present in the anodic oxide films was compressive, and the stress was higher in the alloys with ECAP than without. The compressive internal stress gradually decreased with increasing annealing temperature. Cracks occurred in the anodic oxide film on Al-Mg alloy during initial corrosion. The ECAP produces high internal stresses in the Al-Mg alloy; the stresses remain in the anodic oxide films, increasing the likelihood of cracks. It is assumed that the pitting corrosion is promoted by these cracks as a result of the higher internal stress resulting from the ECAP. The improvement in the pitting corrosion resistance of anodized Al-Mg allov by annealing appears to be attributable to a decrease in the internal stresses in anodic oxide films.

UR - http://www.scopus.com/inward/record.url?scp=58149269556&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=58149269556&partnerID=8YFLogxK

U2 - 10.2320/matertrans.MRA2008230

DO - 10.2320/matertrans.MRA2008230

M3 - Article

AN - SCOPUS:58149269556

VL - 49

SP - 2656

EP - 2663

JO - Materials Transactions

JF - Materials Transactions

SN - 0916-1821

IS - 11

ER -