Effect of doped ceria interlayer on cathode performance of the electrochemical cell using proton conducting oxide

Takaaki Sakai, Shotaro Matsushita, Junji Hyodo, Yuji Okuyama, Maki Matsuka, Tatsumi Ishihara, Hiroshige Matsumoto

研究成果: Contribution to journalArticle査読

6 被引用数 (Scopus)

抄録

Introduction of doped ceria interlayer to cathode/electrolyte interface of the electrochemical cell with proton conducting electrolyte was investigated using thin Ce 0.8Yb 0.2O 2-δ (YbDC) interlayer of about 500 nm thickness. YbDC interlayer conducted a large amount of protons as much as 170 mA cm -2. It was also found that cathode overpotential of the YbDC interlayer cells consistently showed a plateau at about 400 mV, at which that of the non-interlayer cells did not show, suggesting a possibility that cathode reaction is changed by introducing the doped ceria interlayer. This result also indicates that the interlayer showed high activity for cathode reaction when enough cathodic bias was applied. Especially, the interlayer showed high activity for the improvement of poor cathode reaction between SrZr 0.9Y 0.1O 3-α (SZY-91) electrolyte and platinum cathode.

本文言語英語
ページ(範囲)179-184
ページ数6
ジャーナルElectrochimica Acta
75
DOI
出版ステータス出版済み - 7 30 2012

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Electrochemistry

フィンガープリント 「Effect of doped ceria interlayer on cathode performance of the electrochemical cell using proton conducting oxide」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル