Effect of electrolysis conditions on the morphology and corrosion resistance of polyaniline films formed on iron by electropolymerization

Hiroaki Nakano, Keiichi Hayashi, Satoshi Oue, Shigeo Kobayashi

研究成果: ジャーナルへの寄稿記事

抄録

Polyaniline films were formed on an Fe substrate using the oxidative electropolymerization technique at 288 K in aqueous solutions of pH 2 to 10 containing aniline and p-toluenesulfonic and oxalic acids as supporting electrolytes, and the effect of conditions of electrolysis on the morphology and corrosion resistance of the films was investigated. Although the polyaniline films were formed partially in solutions of pH 2 to 4, the formation of films completed and the surface became smooth in solutions of pH 7 to 10. Polyaniline films with a smooth surface and good corrosion resistance were obtained at 8 to 30 A·m-2, while the films obtained at current densities above 50 A·m-2 showed a non-uniform surface morphology and the insufficient corrosion resistance. Films obtained at anode potentials of 0.4 and 0.8 V vs. NHE were not formed completely, and the films formed at an anode potential of 2.0 V exhibited very rough surfaces. Films formed from the solution containing p-toluenesulfonic acid as a supporting electrolyte exfoliated from the Fe substrate following immersion in a 3 mass% NaCl solution for 3 h. Although the films obtained from the solution containing oxalic acid as a supporting electrolyte showed the good adhesion to the substrate, they possessed many defects and pores, and as a result, the improvement in the Fe's corrosion resistance was less. In the solution containing both ptoluenesulfonic and oxalic acids as supporting electrolytes, the Fe coated with polyaniline films showed the good improvements in both corrosion resistance and adhesion.

元の言語英語
ページ(範囲)157-164
ページ数8
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
80
発行部数2
DOI
出版物ステータス出版済み - 1 1 2016

Fingerprint

Electropolymerization
electrolysis
Polyaniline
Electrolysis
corrosion resistance
Corrosion resistance
Iron
iron
Electrolytes
oxalic acid
Oxalic acid
electrolytes
Oxalates
acids
Anodes
adhesion
anodes
polyaniline
Substrates
Adhesion

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

これを引用

@article{57738428bab94038afe2233b5d3e0af7,
title = "Effect of electrolysis conditions on the morphology and corrosion resistance of polyaniline films formed on iron by electropolymerization",
abstract = "Polyaniline films were formed on an Fe substrate using the oxidative electropolymerization technique at 288 K in aqueous solutions of pH 2 to 10 containing aniline and p-toluenesulfonic and oxalic acids as supporting electrolytes, and the effect of conditions of electrolysis on the morphology and corrosion resistance of the films was investigated. Although the polyaniline films were formed partially in solutions of pH 2 to 4, the formation of films completed and the surface became smooth in solutions of pH 7 to 10. Polyaniline films with a smooth surface and good corrosion resistance were obtained at 8 to 30 A·m-2, while the films obtained at current densities above 50 A·m-2 showed a non-uniform surface morphology and the insufficient corrosion resistance. Films obtained at anode potentials of 0.4 and 0.8 V vs. NHE were not formed completely, and the films formed at an anode potential of 2.0 V exhibited very rough surfaces. Films formed from the solution containing p-toluenesulfonic acid as a supporting electrolyte exfoliated from the Fe substrate following immersion in a 3 mass{\%} NaCl solution for 3 h. Although the films obtained from the solution containing oxalic acid as a supporting electrolyte showed the good adhesion to the substrate, they possessed many defects and pores, and as a result, the improvement in the Fe's corrosion resistance was less. In the solution containing both ptoluenesulfonic and oxalic acids as supporting electrolytes, the Fe coated with polyaniline films showed the good improvements in both corrosion resistance and adhesion.",
author = "Hiroaki Nakano and Keiichi Hayashi and Satoshi Oue and Shigeo Kobayashi",
year = "2016",
month = "1",
day = "1",
doi = "10.2320/jinstmet.J2015048",
language = "English",
volume = "80",
pages = "157--164",
journal = "Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals",
issn = "0021-4876",
publisher = "公益社団法人 日本金属学会",
number = "2",

}

TY - JOUR

T1 - Effect of electrolysis conditions on the morphology and corrosion resistance of polyaniline films formed on iron by electropolymerization

AU - Nakano, Hiroaki

AU - Hayashi, Keiichi

AU - Oue, Satoshi

AU - Kobayashi, Shigeo

PY - 2016/1/1

Y1 - 2016/1/1

N2 - Polyaniline films were formed on an Fe substrate using the oxidative electropolymerization technique at 288 K in aqueous solutions of pH 2 to 10 containing aniline and p-toluenesulfonic and oxalic acids as supporting electrolytes, and the effect of conditions of electrolysis on the morphology and corrosion resistance of the films was investigated. Although the polyaniline films were formed partially in solutions of pH 2 to 4, the formation of films completed and the surface became smooth in solutions of pH 7 to 10. Polyaniline films with a smooth surface and good corrosion resistance were obtained at 8 to 30 A·m-2, while the films obtained at current densities above 50 A·m-2 showed a non-uniform surface morphology and the insufficient corrosion resistance. Films obtained at anode potentials of 0.4 and 0.8 V vs. NHE were not formed completely, and the films formed at an anode potential of 2.0 V exhibited very rough surfaces. Films formed from the solution containing p-toluenesulfonic acid as a supporting electrolyte exfoliated from the Fe substrate following immersion in a 3 mass% NaCl solution for 3 h. Although the films obtained from the solution containing oxalic acid as a supporting electrolyte showed the good adhesion to the substrate, they possessed many defects and pores, and as a result, the improvement in the Fe's corrosion resistance was less. In the solution containing both ptoluenesulfonic and oxalic acids as supporting electrolytes, the Fe coated with polyaniline films showed the good improvements in both corrosion resistance and adhesion.

AB - Polyaniline films were formed on an Fe substrate using the oxidative electropolymerization technique at 288 K in aqueous solutions of pH 2 to 10 containing aniline and p-toluenesulfonic and oxalic acids as supporting electrolytes, and the effect of conditions of electrolysis on the morphology and corrosion resistance of the films was investigated. Although the polyaniline films were formed partially in solutions of pH 2 to 4, the formation of films completed and the surface became smooth in solutions of pH 7 to 10. Polyaniline films with a smooth surface and good corrosion resistance were obtained at 8 to 30 A·m-2, while the films obtained at current densities above 50 A·m-2 showed a non-uniform surface morphology and the insufficient corrosion resistance. Films obtained at anode potentials of 0.4 and 0.8 V vs. NHE were not formed completely, and the films formed at an anode potential of 2.0 V exhibited very rough surfaces. Films formed from the solution containing p-toluenesulfonic acid as a supporting electrolyte exfoliated from the Fe substrate following immersion in a 3 mass% NaCl solution for 3 h. Although the films obtained from the solution containing oxalic acid as a supporting electrolyte showed the good adhesion to the substrate, they possessed many defects and pores, and as a result, the improvement in the Fe's corrosion resistance was less. In the solution containing both ptoluenesulfonic and oxalic acids as supporting electrolytes, the Fe coated with polyaniline films showed the good improvements in both corrosion resistance and adhesion.

UR - http://www.scopus.com/inward/record.url?scp=84982306900&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84982306900&partnerID=8YFLogxK

U2 - 10.2320/jinstmet.J2015048

DO - 10.2320/jinstmet.J2015048

M3 - Article

VL - 80

SP - 157

EP - 164

JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals

SN - 0021-4876

IS - 2

ER -