Effect of heating temperature on tritium retention in stainless steel type 316 L

M. Matsuyama, H. Zushi, K. Tokunaga, A. Kuzmin, K. Hanada

研究成果: ジャーナルへの寄稿学術誌査読

5 被引用数 (Scopus)

抄録

Dependence of heating temperature on tritium retention behavior in stainless steel type 316 L (SS316L) has been examined about each process of degassing and tritium exposure. Two kinds of SS316L samples were employed: bare SS316L and plasma-exposed SS316L. The amount of tritium retained in surface layers of a sample was nondestructively measured by β-ray-induced X-ray spectrometry, and changes in the surface state with heating in vacuum were analyzed by X-ray photoelectron spectroscopy (XPS). Significant increase in tritium retention in bare SS316L samples appeared in a degassing temperature region above 600 K. Similar tendency of tritium retention was observed for the plasma-exposed sample. It was seen that the degassing process prior to tritium exposure significantly influenced to the tritium retention behavior. Furthermore, it was suggested from surface analysis by XPS that chemical states of SS316L surface at high temperatures play an important role for tritium retention behavior.

本文言語英語
ページ(範囲)52-59
ページ数8
ジャーナルNuclear Materials and Energy
16
DOI
出版ステータス出版済み - 8月 2018

!!!All Science Journal Classification (ASJC) codes

  • 核物理学および高エネルギー物理学
  • 材料科学(その他)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「Effect of heating temperature on tritium retention in stainless steel type 316 L」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル