Effect of la2o3 addition on interface chemistry between 4YSZ top layer and Ni based alloy bond coat in thermal barrier coating by EB PVD

Chan Young Park, Young Hwan Yang, Seong Won Kim, Sung Min Lee, Hyung Tae Kim, Byung Koog Jang, Dae Soon Lim, Yoon Suk Oh

研究成果: ジャーナルへの寄稿記事

2 引用 (Scopus)

抄録

The effect of a 5 mol% La203 addition on the forming behavior and compositional variation at interface between a 4 mol% Yttria (Y203) stabilized Zr02 (4YSZ) top coat and bond coat (NiCrAlY,) as a thermal barrier coating (TBC) has been investigated. Top coats were deposited by electron beam physical vapor deposition (EB PVD) onto a super alloy (Ni-Cr-Co-Al) substrate without pre-oxidation of the bond coat. Top coats are found to consist of dense columnar grains with a thin interdiffusion layer between metallic bond coats. In the as-received 4YSZ coating, a thin interdiffusion zone at the interface between the top and bond coats was found to consist of a Ni-Zr intermetallic compound with a reduced quantity of Y. Al or O elements. On the other hand, in the case of an interdiffusion area of 5 mol% La2O3-added 4YSZ coating, it was found that the complicated composition and structure with La-added YSZ and Ni-Al rich compounds separately. The thermal conductivity of 5 mol% La203-added 4YSZ coating (∼ 1.6 W/m - k at 1100 °C) was lower than a 4YSZ coating (∼ 3.2 W/m • k at 1100 °C) alone.

元の言語英語
ページ(範囲)8659-8664
ページ数6
ジャーナルJournal of nanoscience and nanotechnology
14
発行部数11
DOI
出版物ステータス出版済み - 11 1 2014

Fingerprint

Thermal Conductivity
Thermal barrier coatings
Physical vapor deposition
Electron beams
Hot Temperature
vapor deposition
electron beams
Electrons
chemistry
coatings
Coatings
Interdiffusion (solids)
Yttrium oxide
Intermetallics
Thermal conductivity
yttria-stabilized zirconia
intermetallics
thermal conductivity
Oxidation
yttria

All Science Journal Classification (ASJC) codes

  • Bioengineering
  • Chemistry(all)
  • Biomedical Engineering
  • Materials Science(all)
  • Condensed Matter Physics

これを引用

Effect of la2o3 addition on interface chemistry between 4YSZ top layer and Ni based alloy bond coat in thermal barrier coating by EB PVD. / Park, Chan Young; Yang, Young Hwan; Kim, Seong Won; Lee, Sung Min; Kim, Hyung Tae; Jang, Byung Koog; Lim, Dae Soon; Oh, Yoon Suk.

:: Journal of nanoscience and nanotechnology, 巻 14, 番号 11, 01.11.2014, p. 8659-8664.

研究成果: ジャーナルへの寄稿記事

Park, Chan Young ; Yang, Young Hwan ; Kim, Seong Won ; Lee, Sung Min ; Kim, Hyung Tae ; Jang, Byung Koog ; Lim, Dae Soon ; Oh, Yoon Suk. / Effect of la2o3 addition on interface chemistry between 4YSZ top layer and Ni based alloy bond coat in thermal barrier coating by EB PVD. :: Journal of nanoscience and nanotechnology. 2014 ; 巻 14, 番号 11. pp. 8659-8664.
@article{7318fc3fa6f04af2b259cdb7ccce3340,
title = "Effect of la2o3 addition on interface chemistry between 4YSZ top layer and Ni based alloy bond coat in thermal barrier coating by EB PVD",
abstract = "The effect of a 5 mol{\%} La203 addition on the forming behavior and compositional variation at interface between a 4 mol{\%} Yttria (Y203) stabilized Zr02 (4YSZ) top coat and bond coat (NiCrAlY,) as a thermal barrier coating (TBC) has been investigated. Top coats were deposited by electron beam physical vapor deposition (EB PVD) onto a super alloy (Ni-Cr-Co-Al) substrate without pre-oxidation of the bond coat. Top coats are found to consist of dense columnar grains with a thin interdiffusion layer between metallic bond coats. In the as-received 4YSZ coating, a thin interdiffusion zone at the interface between the top and bond coats was found to consist of a Ni-Zr intermetallic compound with a reduced quantity of Y. Al or O elements. On the other hand, in the case of an interdiffusion area of 5 mol{\%} La2O3-added 4YSZ coating, it was found that the complicated composition and structure with La-added YSZ and Ni-Al rich compounds separately. The thermal conductivity of 5 mol{\%} La203-added 4YSZ coating (∼ 1.6 W/m - k at 1100 °C) was lower than a 4YSZ coating (∼ 3.2 W/m • k at 1100 °C) alone.",
author = "Park, {Chan Young} and Yang, {Young Hwan} and Kim, {Seong Won} and Lee, {Sung Min} and Kim, {Hyung Tae} and Jang, {Byung Koog} and Lim, {Dae Soon} and Oh, {Yoon Suk}",
year = "2014",
month = "11",
day = "1",
doi = "10.1166/jnn.2014.10000",
language = "English",
volume = "14",
pages = "8659--8664",
journal = "Journal of Nanoscience and Nanotechnology",
issn = "1533-4880",
publisher = "American Scientific Publishers",
number = "11",

}

TY - JOUR

T1 - Effect of la2o3 addition on interface chemistry between 4YSZ top layer and Ni based alloy bond coat in thermal barrier coating by EB PVD

AU - Park, Chan Young

AU - Yang, Young Hwan

AU - Kim, Seong Won

AU - Lee, Sung Min

AU - Kim, Hyung Tae

AU - Jang, Byung Koog

AU - Lim, Dae Soon

AU - Oh, Yoon Suk

PY - 2014/11/1

Y1 - 2014/11/1

N2 - The effect of a 5 mol% La203 addition on the forming behavior and compositional variation at interface between a 4 mol% Yttria (Y203) stabilized Zr02 (4YSZ) top coat and bond coat (NiCrAlY,) as a thermal barrier coating (TBC) has been investigated. Top coats were deposited by electron beam physical vapor deposition (EB PVD) onto a super alloy (Ni-Cr-Co-Al) substrate without pre-oxidation of the bond coat. Top coats are found to consist of dense columnar grains with a thin interdiffusion layer between metallic bond coats. In the as-received 4YSZ coating, a thin interdiffusion zone at the interface between the top and bond coats was found to consist of a Ni-Zr intermetallic compound with a reduced quantity of Y. Al or O elements. On the other hand, in the case of an interdiffusion area of 5 mol% La2O3-added 4YSZ coating, it was found that the complicated composition and structure with La-added YSZ and Ni-Al rich compounds separately. The thermal conductivity of 5 mol% La203-added 4YSZ coating (∼ 1.6 W/m - k at 1100 °C) was lower than a 4YSZ coating (∼ 3.2 W/m • k at 1100 °C) alone.

AB - The effect of a 5 mol% La203 addition on the forming behavior and compositional variation at interface between a 4 mol% Yttria (Y203) stabilized Zr02 (4YSZ) top coat and bond coat (NiCrAlY,) as a thermal barrier coating (TBC) has been investigated. Top coats were deposited by electron beam physical vapor deposition (EB PVD) onto a super alloy (Ni-Cr-Co-Al) substrate without pre-oxidation of the bond coat. Top coats are found to consist of dense columnar grains with a thin interdiffusion layer between metallic bond coats. In the as-received 4YSZ coating, a thin interdiffusion zone at the interface between the top and bond coats was found to consist of a Ni-Zr intermetallic compound with a reduced quantity of Y. Al or O elements. On the other hand, in the case of an interdiffusion area of 5 mol% La2O3-added 4YSZ coating, it was found that the complicated composition and structure with La-added YSZ and Ni-Al rich compounds separately. The thermal conductivity of 5 mol% La203-added 4YSZ coating (∼ 1.6 W/m - k at 1100 °C) was lower than a 4YSZ coating (∼ 3.2 W/m • k at 1100 °C) alone.

UR - http://www.scopus.com/inward/record.url?scp=84908431741&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84908431741&partnerID=8YFLogxK

U2 - 10.1166/jnn.2014.10000

DO - 10.1166/jnn.2014.10000

M3 - Article

AN - SCOPUS:84908431741

VL - 14

SP - 8659

EP - 8664

JO - Journal of Nanoscience and Nanotechnology

JF - Journal of Nanoscience and Nanotechnology

SN - 1533-4880

IS - 11

ER -