Effect of notch shape and absorbed hydrogen on the fatigue fracture in two-step stress test below fatigue limit

Yoshiyuki Kondo, Masanobu Kubota, Hikaru Eda

    研究成果: Contribution to journalArticle査読

    抄録

    It is usually regarded as a common understanding that fatigue failure would not occur if all stresses were kept below fatigue limit diagram. However, it was shown that fatigue failure occurred in some special cases of variable amplitude loading condition even when all stresses were kept below fatigue limit diagram in the case of small-notched specimen. The cause of such a phenomenon was examined using two-step stress pattern for low alloy steel SCM440H. In the case of constant stress amplitude loading, non-propagating crack was formed only at low mean stress region and not formed at high mean stress. However, in the case of two-step stress pattern in which the first step stress was chosen as R = -1 and the second step stress was with high mean stress, a non-propagating crack was formed by the first step stress. This crack functioned as a pre-crack for the second step stress with high mean stress. In this study, the effect of notch shape was examined. The effect of absorbed hydrogen was also investigated. Absorption of 0.3 ppm hydrogen caused more reduction of fatigue limit.

    本文言語英語
    ページ(範囲)1358-1365
    ページ数8
    ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
    74
    10
    DOI
    出版ステータス出版済み - 10 2008

    All Science Journal Classification (ASJC) codes

    • 材料科学(全般)
    • 材料力学
    • 機械工学

    フィンガープリント

    「Effect of notch shape and absorbed hydrogen on the fatigue fracture in two-step stress test below fatigue limit」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル