水酸化カリウムを用いたジンケート浴からの亜鉛の電析挙動とその微細構造に及ぼす有機添加剤の影響

Kenta Fukumoto, Satoshi Oue, Tsukasa Niwa, Yoshiharu Kikuchi, Shinya Akamatsu, Hiroaki Nakano

    研究成果: Contribution to journalArticle査読

    抄録

    Electrodeposition of Zn was performed on an Fe electrode at a current density of 50–5000 A·m−2 and a charge of 4 × 104 C·m−2 in an unagitated zincate solution at 313 K containing 0.62 mol·dm−3 of ZnO, 4.0 mol·dm−3 of KOH or NaOH, and organic additives. The effects of KOH and NaOH on the deposition behavior of Zn in solution containing organic additives and the microstructure of the deposits were investigated. In solution containing a quaternary ammonium cation (PQ) and a quaternary ammonium salt with a benzene ring (QA), the current efficiency for Zn deposition at high current density region of 1000 to 5000 A·m−2 to produce the glossy films was higher with KOH than that with NaOH. At high current densities above 1000 A·m−2, Zn deposition approaches the diffusion limitation of ZnO22− ions. With additions of PQ and QA, the diffusion of ZnO22− ions was significantly suppressed, and the degree of suppression was smaller with KOH than that with NaOH. The polarization resistance at 200 A·m−2 investigated by AC impedance revealed that the adsorption ability of PQ and QA onto the cathode was smaller with KOH than that with NaOH. Since the suppression effect of additives on the Zn deposition is smaller with KOH than that with NaOH, the current efficiency for Zn deposition at high current density region is larger with KOH. The upper limit of current density to produce the glossy films was smaller with KOH than that with NaOH, and the spongy thin films were partially observed on the platelets crystals obtained at high current density in KOH solution. The content of C resulting from the additives in deposited Zn was smaller with KOH. These phenomena are attributed to the adsorption ability of PQ and QA onto the cathode being smaller with KOH.

    寄稿の翻訳タイトルEffect of organic additives on electrodeposition behavior of ZN from zincate solution containing potassium hydroxide and its micro structure
    本文言語日本語
    ページ(範囲)59-66
    ページ数8
    ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
    85
    2
    DOI
    出版ステータス出版済み - 2021

    All Science Journal Classification (ASJC) codes

    • 凝縮系物理学
    • 材料力学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「水酸化カリウムを用いたジンケート浴からの亜鉛の電析挙動とその微細構造に及ぼす有機添加剤の影響」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル