Effect of substitution of Fe and Ni for Co in the synthesis of Mg2Co compound using the mechanical alloying method

Jean Louis Bobet, Etsuo Akiba, B. Darriet

研究成果: Contribution to journalArticle査読

24 被引用数 (Scopus)

抄録

The influence of the elaboration route of Mg2Co1-xMx (M = Fe or Ni and x≤0.3) hydrogen storage alloy was investigated. When Co was replaced by Fe, the formation of `Mg2Co' (containing a very small amount of Fe) was observed after about 60 h of ball milling, but the yield of formation was lower. Increasing milling time just led to an amorphization of the `Mg2Co' compound. We also observed, that as expected, no new compound was formed between Mg and Fe. Annealing of unmilled products did not lead to any new compounds and annealing of milled products just led to the crystallization of the existing compounds. When cobalt was replaced by nickel, the major difference was the formation, after annealing, of the Mg2Ni compound. This difference is attributed to the higher stability of Mg2Ni compared to that of `Mg2Co'. The yield of the `Mg2Co' phase was higher than that with Fe and that without any adding element.

本文言語英語
ページ(範囲)192-198
ページ数7
ジャーナルJournal of Alloys and Compounds
297
1-2
DOI
出版ステータス出版済み - 2 2 2000
外部発表はい

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Effect of substitution of Fe and Ni for Co in the synthesis of Mg<sub>2</sub>Co compound using the mechanical alloying method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル