Effect of thermo-mechanical treatment on ridging behavior and cube-oriented grain formation process in 6111 aluminum alloy

Ken Ichi Ikeda, Yukimasa Miyata, Takahiro Yoshihara, Naoki Takata, Hideharu Nakashima

研究成果: ジャーナルへの寄稿学術誌査読

抄録

Al-Mg-Si alloys are suitable materials for automotive body application because of a good formability, a good corrosion resistance and a satisfactory strengthening. However, it is well known that when some kinds of Al-Mg-Si alloy sheets are stretched along the transverse direction, rope-like profiles (ridging/roping) parallel to the rolling direction develop on the surface. The purpose of this study is to clarify the ridging development in Al-Mg-Si alloy (6111 aluminum alloy). The effect of thermo-mechanical treatment on ridging development was investigated by 3D profile microscope and SEM/EBSD method. Rope-like profiles tended to develop remarkably in the hot-rolled and intermediate-annealed sheets. In highly ridging developed sample, there were many bands of cube-oriented grains (cube bands). Therefore, in this study, the cube-oriented grain formation process was also investigated by SEM/EBSD and TEM observation. Microstructure observations revealed that cube-oriented grains formed during the hot rolling process could remain due to rod-like precipitates in grain. And then, these cube-oriented grains were grown along the rolling direction during the intermediate annealing. Crystal orientation analysis shows the stored energy of the cube-oriented grains in the cold rolled sheet was lower than that of other-oriented grains. Therefore, we concluded that cube bands are preferentially formed during solutionized treatment.

本文言語英語
ページ(範囲)353-360
ページ数8
ジャーナルKeikinzoku/Journal of Japan Institute of Light Metals
64
8
DOI
出版ステータス出版済み - 2014

!!!All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Effect of thermo-mechanical treatment on ridging behavior and cube-oriented grain formation process in 6111 aluminum alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル