Effect of V on the tensile strength of sintered Cr-Mo alloyed steel powder compacts

Shigeru Unami, Osamu Furukimi, Satoshi Uenosono, Kuniaki Ogura

    研究成果: Contribution to journalArticle査読

    3 被引用数 (Scopus)

    抄録

    A prealloyed 1Cr-0.3Mo-0.3V(mass%) steel powder was developed to obtain the high strength sintered compacts. This new sintered 1Cr-0.3Mo-0.3V powder compact, which is Mn-less, made it possible to extend the range of the cooling rate after sintering to attain higher strength than that of sintered 1Cr-0.3Mo steel, and gave a tensile strength of more than 800 MPa and a rotating bending fatigue strength of 310MPa at the cooling rates of 1 to 30°C/min. The wide range of cooling rates at which high strength can be obtained was attributed to a decrease in hardenability and the production of a fine pearlite structure by V addition. The improvement of the strength for the compacts added V is attributed to the precipitation hardening of V carbonitrides, as well as a narrow pearlite lamellar spacing.

    本文言語英語
    ページ(範囲)1106-1110
    ページ数5
    ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
    43
    9
    DOI
    出版ステータス出版済み - 9 1996

    All Science Journal Classification (ASJC) codes

    • 機械工学
    • 産業および生産工学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Effect of V on the tensile strength of sintered Cr-Mo alloyed steel powder compacts」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル