Effect of vanadium and niobium on creep strength in 10% chromium R steel analyzed by STEM-EDS

Masatoshi Mitsuhara, Yu Yoshida, Ken Ichi Ikeda, Hideharu Nakashima, Takashi Wakai

研究成果: 著書/レポートタイプへの貢献会議での発言

抜粋

The effect of vanadium and niobium on creep strengthening was studied in 10% chromium steels. Eleven kinds of samples which varied the additive amounts of vanadium and niobium were prepared. From the creep deformation behavior of them, the threshold stresses were estimated. The distribution maps of precipitates were obtained by STEM-EDS. In a steel with added 0.06% vanadium where no particles were observed in the lath, creep strength was slightly increased, indicating that it was not strengthened by a particle hardening effect in the lath. Lump-shaped precipitates and film-shaped precipitates including chromium and vanadium, which were observed on lath boundaries in the steel with added vanadium, are expected to inhibit the lath boundaries from migrating. This inhibition is the mechanism of the improvement in the steel with added vanadium. In the case of steels with added niobium, creep strength was found to be increased by dispersion hardening due to fine precipitates in the lath. The threshold stress was quantitatively estimated depending on the particle spacing. The estimated threshold stress corresponded to the one obtained by the creep deformation behavior. These results revealed that vanadium and niobium each have a role in improving creep strength. In steels with added both vanadium and niobium, the effect on creep strength was expressed by the sum of the effects due to each element, which were the retardation of the lath boundary migrations and the pinning of the dislocations in the lath.

元の言語英語
ホスト出版物のタイトル2007 Proceedings of the ASME Pressure Vessels and Piping Conference - 8th International Conference on Creep and Fatigue at Elevated Temperatures - CREEP8
ページ51-55
ページ数5
DOI
出版物ステータス出版済み - 5 19 2008
イベント2007 ASME Pressure Vessels and Piping Conference - 8th International Conference on Creep and Fatigue at Elevated Temperatures, PVP-2007/CREEP8 - San Antonio, TX, 米国
継続期間: 7 22 20077 26 2007

その他

その他2007 ASME Pressure Vessels and Piping Conference - 8th International Conference on Creep and Fatigue at Elevated Temperatures, PVP-2007/CREEP8
米国
San Antonio, TX
期間7/22/077/26/07

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering

これを引用

Mitsuhara, M., Yoshida, Y., Ikeda, K. I., Nakashima, H., & Wakai, T. (2008). Effect of vanadium and niobium on creep strength in 10% chromium R steel analyzed by STEM-EDS. : 2007 Proceedings of the ASME Pressure Vessels and Piping Conference - 8th International Conference on Creep and Fatigue at Elevated Temperatures - CREEP8 (pp. 51-55) https://doi.org/10.1115/CREEP2007-26746