Effects of ball milling and additives on dehydriding behaviors of well-crystallized Mg(BH4)2

H. W. Li, K. Kikuchi, Y. Nakamori, K. Miwa, S. Towata, S. Orimo

研究成果: ジャーナルへの寄稿学術誌査読

165 被引用数 (Scopus)

抄録

Well-crystallized Mg(BH4)2 was chemically synthesized and the effect of ball milling and Ti-based additives on the dehydriding properties were investigated. The dehydriding reaction of the as-synthesized Mg(BH4)2 initiates at approximately 535 K and about 13.7 mass% of hydrogen is desorbed. Compared with the as-synthesized Mg(BH4)2, few changes are observed in the samples after ball milling, while the initial dehydriding temperature of Mg(BH4)2 is significantly reduced by the addition of TiCl3, i.e. from 535 K down to 361 K.

本文言語英語
ページ(範囲)679-682
ページ数4
ジャーナルScripta Materialia
57
8
DOI
出版ステータス出版済み - 10月 2007
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学
  • 金属および合金

フィンガープリント

「Effects of ball milling and additives on dehydriding behaviors of well-crystallized Mg(BH4)2」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル