Effects of heat-treatment conditions on microstructure of multi-coating Y123 films deposited by advanced TFA-MOD method

J. S. Matsuda, Y. Tokunaga, R. Teranishi, H. Fuji, A. Kaneko, S. Asada, T. Honjo, A. Yajima, Y. Iijima, T. Saitoh, T. Izumi, Y. Shiohara

研究成果: ジャーナルへの寄稿学術誌査読

34 被引用数 (Scopus)

抄録

YBa2Cu3O7-δ (Y123) films were deposited under various water partial pressures (PH2O) in the crystallization process by the advanced metalorganic deposition (MOD) method using trifluoroacetates. Microstructures of the films were evaluated by means of transmission electron microscopy. As a result, in the Y123 film crystallized under lower PH2O such as 2.1%, large pores were remarkably observed. Furthermore, there were many amorphous layers of a non-superconducting phase in this film. In contrast, small pores were distributed in the films deposited under higher PH2O. Considering that the critical current (I C) values become higher as PH2O increases, existence of large pores and non-superconducting phase crystals causes to reduce I C. Through the investigation of the microstructure of the films quenched during the crystallization process, it was found that the pores in the film are generated by reaction of the non-superconducting phases, which are trapped in the growing Y123 film afterwards, to transform to Y123 with accompanied by the volume reduction of about 30%. The sizes of the entrapped phase crystals in Y123 film depend on the PH2O and it may determine the pore sizes in the final film.

本文言語英語
ページ(範囲)890-895
ページ数6
ジャーナルPhysica C: Superconductivity and its applications
412-414
SPEC. ISS.
DOI
出版ステータス出版済み - 10月 2004
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Effects of heat-treatment conditions on microstructure of multi-coating Y123 films deposited by advanced TFA-MOD method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル