Effects of Hydrogen and Pre-strain on Tensile Properties of Carbon Steel STPG370 (0.19 C-0.21 Si-0.56Mn, mass%) for 1 MPa Hydrogen Pipelines

Shi Nishiguchi, Hihiro Fukushima, Saburo Matsuoka, Yukitaka Murakami

研究成果: Contribution to journalArticle査読

11 被引用数 (Scopus)

抄録

The effects of hydrogen and pre-strain on tensile properties of JIS-STPG 370 carbon steel pipe for hydrogen pipelines were investigated. In order to pre-charge hydrogen, the specimens were immersed in a 20 mass% aqueous solution of ammonium thiocyanate at 313 Κfor 48 h. The hydrogen content increased with increasing the pre-strain. The reduction of area of hydrogen-charged specimens decreased with pre-strain. Although pearlite cracks were formed both in the uncharged and hydrogen-charged specimens, the initiation of pearlite cracks occurred at the lower true strain in the hydrogen-charged specimen. Furthermore, the pearlite cracks grew in the direction perpendic-ular to the loading axis in the hydrogen-charged specimen. The experimental evidences are shown to explain the mechanism of the initiation and growth of pearlite cracks in the hydrogen-charged specimen by the hydrogen enhanced localized plasticity model rather than the lattice decohesion model.

本文言語英語
ページ(範囲)1016-1025
ページ数10
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
74
743
DOI
出版ステータス出版済み - 1 1 2008

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Effects of Hydrogen and Pre-strain on Tensile Properties of Carbon Steel STPG370 (0.19 C-0.21 Si-0.56Mn, mass%) for 1 MPa Hydrogen Pipelines」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル