Effects of internal hydrogen on fatigue strength of commercially pure titanium

Hideaki Nishikawa, Yasuji Oda, Hiroshi Noguchi

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

1 被引用数 (Scopus)

抄録

Commercially Pure Titanium (CP-Ti) usually contains a few tens of ppm hydrogen. In order to investigate the effect of such internal hydrogen on the fatigue characteristics, rotating bending fatigue tests were carried out on two kinds of specimen with different hydrogen contents: one contains 34 ppm but the other 3 ppm. The amount of internal hydrogen was controlled by changing the annealing conditions. The fatigue process was successively observed by a replication technique. The higher hydrogen content specimen showed a longer fatigue life, longer crack initiation life and higher fatigue limit than those of the lower hydrogen specimen. No specimen showed any particular fatigue crack growth behavior related to hydrogen content, whereas the crack initiation behavior differed somewhat. The fatigue-crack initiation site of the higher hydrogen content specimen with a longer fatigue life preferred the interior of a grain. On the other hand, that of the lower hydrogen specimen preferred the neighborhood of a grain boundary.

本文言語英語
ホスト出版物のタイトル17th European Conference on Fracture 2008: Multilevel Approach to Fracture of Materials, Components and Structures
ページ1289-1296
ページ数8
2
出版ステータス出版済み - 2008
イベント17th European Conference on Fracture 2008: Multilevel Approach to Fracture of Materials, Components and Structures, ECF17 - Brno, チェコ共和国
継続期間: 9 2 20089 5 2008

その他

その他17th European Conference on Fracture 2008: Multilevel Approach to Fracture of Materials, Components and Structures, ECF17
国/地域チェコ共和国
CityBrno
Period9/2/089/5/08

All Science Journal Classification (ASJC) codes

  • 土木構造工学

フィンガープリント

「Effects of internal hydrogen on fatigue strength of commercially pure titanium」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル