Electrochemical performance of an all-solid-state lithium-oxygen battery under humidified oxygen

Y. Suzuki, K. Watanabe, S. Sakuma, N. Imanishi

研究成果: Contribution to journalArticle査読

11 被引用数 (Scopus)

抄録

The electrochemical performance of an all-solid-state lithium-oxygen battery was examined using a platinum patterned electrode with a lithium conducting solid electrolyte under a humidified O2 atmosphere. The cell consisted of a lithium metal anode, a protective layer of polyethylene oxide with Li(CF3SO2)2N, a lithium-conducting solid electrolyte of Li1 + x + yAlx(Ge,Ti)2 - xSiyP3 - yO12, and a sputtered platinum stripe-patterned air electrode. The open circuit voltage (OCV) of the virgin cell was 3.5 V under humidified O2 and decreased to 3.2 V after slight discharge, which is comparable with that under dry O2 (2.4 V). The cell was successfully discharged and charged at 0.1 mA cm- 2 and 60 °C. A reaction product was observed on the platinum electrode; however, it could not be identified by X-ray diffraction analysis or Raman spectroscopy, which indicated it was amorphous. Nano-secondary ion mass spectrometry (SIMS) analysis suggested that the reaction product contains Li, H, and O.

本文言語英語
ページ(範囲)72-76
ページ数5
ジャーナルSolid State Ionics
289
DOI
出版ステータス出版済み - 6 1 2016
外部発表はい

All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Electrochemical performance of an all-solid-state lithium-oxygen battery under humidified oxygen」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル