Electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution containing ethylenediamine

Hiroaki Nakano, Shingo Arakawa, Satoshi Oue, Shigeo Kobayashi

研究成果: ジャーナルへの寄稿記事

抄録

Electrodeposition behavior of Zn-Ni alloys was investigated at current densities of 5-500 A·m-2 and a charge of 5×104 C·m-2 in an unagitated zincate solution containing ethylenediamine, which forms a stable complex with Ni2+ ions at 308 K, and was compared with that from the solution containing triethanolamine. In a solution containing triethanolamine, the Zn-Ni alloy exhibited normal codeposition at low current densities, wherein electrochemically more noble Ni deposited preferentially and it exhibited anomalous codeposition at high current densities, wherein less noble Zn deposited preferentially, while in a solution containing ethylenediamine, it exhibited anomalous codeposition at high current densities, however, even at low current densities, the Ni content in deposit was almost identical with the composition reference line, showing the behavior close to anomalous codeposition. In a solution containing ethylenediamine, Ni deposition and H2 evolution were significantly suppressed in the larger region of current densities, showing the formation of an inhibitor for deposition, which results from Zn2+ ions in the cathode layer. The dependence of current efficiency for alloy deposition on the current density was smaller in a solution containing ethylenediamine than triethanolamine. In a solution containing triethanolamine, the underpotential deposition of Zn apparently occurred with Ni, while in a solution containing ethylenediamine, the underpotential deposition of Zn never occurred because Ni deposition was suppressed by the coexistence of Zn2+ ions even at low current densities. The throwing power of Zn-Ni alloy was better in a solution containing ethylenediamine than triethanolamine.

元の言語英語
ページ(範囲)35-41
ページ数7
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
99
発行部数6
DOI
出版物ステータス出版済み - 6 18 2013

Fingerprint

ethylenediamine
Electrodeposition
electrodeposition
Triethanolamine
Current density
current density
low currents
Ions
high current
throwing
ions

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Physical and Theoretical Chemistry
  • Metals and Alloys
  • Materials Chemistry

これを引用

Electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution containing ethylenediamine. / Nakano, Hiroaki; Arakawa, Shingo; Oue, Satoshi; Kobayashi, Shigeo.

:: Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan, 巻 99, 番号 6, 18.06.2013, p. 35-41.

研究成果: ジャーナルへの寄稿記事

@article{f1d49c30851e4042beda0b616e86fe88,
title = "Electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution containing ethylenediamine",
abstract = "Electrodeposition behavior of Zn-Ni alloys was investigated at current densities of 5-500 A·m-2 and a charge of 5×104 C·m-2 in an unagitated zincate solution containing ethylenediamine, which forms a stable complex with Ni2+ ions at 308 K, and was compared with that from the solution containing triethanolamine. In a solution containing triethanolamine, the Zn-Ni alloy exhibited normal codeposition at low current densities, wherein electrochemically more noble Ni deposited preferentially and it exhibited anomalous codeposition at high current densities, wherein less noble Zn deposited preferentially, while in a solution containing ethylenediamine, it exhibited anomalous codeposition at high current densities, however, even at low current densities, the Ni content in deposit was almost identical with the composition reference line, showing the behavior close to anomalous codeposition. In a solution containing ethylenediamine, Ni deposition and H2 evolution were significantly suppressed in the larger region of current densities, showing the formation of an inhibitor for deposition, which results from Zn2+ ions in the cathode layer. The dependence of current efficiency for alloy deposition on the current density was smaller in a solution containing ethylenediamine than triethanolamine. In a solution containing triethanolamine, the underpotential deposition of Zn apparently occurred with Ni, while in a solution containing ethylenediamine, the underpotential deposition of Zn never occurred because Ni deposition was suppressed by the coexistence of Zn2+ ions even at low current densities. The throwing power of Zn-Ni alloy was better in a solution containing ethylenediamine than triethanolamine.",
author = "Hiroaki Nakano and Shingo Arakawa and Satoshi Oue and Shigeo Kobayashi",
year = "2013",
month = "6",
day = "18",
doi = "10.2355/tetsutohagane.99.425",
language = "English",
volume = "99",
pages = "35--41",
journal = "Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan",
issn = "0021-1575",
publisher = "一般社団法人 日本鉄鋼協会",
number = "6",

}

TY - JOUR

T1 - Electrodeposition behavior of Zn-Ni alloy from alkaline zincate solution containing ethylenediamine

AU - Nakano, Hiroaki

AU - Arakawa, Shingo

AU - Oue, Satoshi

AU - Kobayashi, Shigeo

PY - 2013/6/18

Y1 - 2013/6/18

N2 - Electrodeposition behavior of Zn-Ni alloys was investigated at current densities of 5-500 A·m-2 and a charge of 5×104 C·m-2 in an unagitated zincate solution containing ethylenediamine, which forms a stable complex with Ni2+ ions at 308 K, and was compared with that from the solution containing triethanolamine. In a solution containing triethanolamine, the Zn-Ni alloy exhibited normal codeposition at low current densities, wherein electrochemically more noble Ni deposited preferentially and it exhibited anomalous codeposition at high current densities, wherein less noble Zn deposited preferentially, while in a solution containing ethylenediamine, it exhibited anomalous codeposition at high current densities, however, even at low current densities, the Ni content in deposit was almost identical with the composition reference line, showing the behavior close to anomalous codeposition. In a solution containing ethylenediamine, Ni deposition and H2 evolution were significantly suppressed in the larger region of current densities, showing the formation of an inhibitor for deposition, which results from Zn2+ ions in the cathode layer. The dependence of current efficiency for alloy deposition on the current density was smaller in a solution containing ethylenediamine than triethanolamine. In a solution containing triethanolamine, the underpotential deposition of Zn apparently occurred with Ni, while in a solution containing ethylenediamine, the underpotential deposition of Zn never occurred because Ni deposition was suppressed by the coexistence of Zn2+ ions even at low current densities. The throwing power of Zn-Ni alloy was better in a solution containing ethylenediamine than triethanolamine.

AB - Electrodeposition behavior of Zn-Ni alloys was investigated at current densities of 5-500 A·m-2 and a charge of 5×104 C·m-2 in an unagitated zincate solution containing ethylenediamine, which forms a stable complex with Ni2+ ions at 308 K, and was compared with that from the solution containing triethanolamine. In a solution containing triethanolamine, the Zn-Ni alloy exhibited normal codeposition at low current densities, wherein electrochemically more noble Ni deposited preferentially and it exhibited anomalous codeposition at high current densities, wherein less noble Zn deposited preferentially, while in a solution containing ethylenediamine, it exhibited anomalous codeposition at high current densities, however, even at low current densities, the Ni content in deposit was almost identical with the composition reference line, showing the behavior close to anomalous codeposition. In a solution containing ethylenediamine, Ni deposition and H2 evolution were significantly suppressed in the larger region of current densities, showing the formation of an inhibitor for deposition, which results from Zn2+ ions in the cathode layer. The dependence of current efficiency for alloy deposition on the current density was smaller in a solution containing ethylenediamine than triethanolamine. In a solution containing triethanolamine, the underpotential deposition of Zn apparently occurred with Ni, while in a solution containing ethylenediamine, the underpotential deposition of Zn never occurred because Ni deposition was suppressed by the coexistence of Zn2+ ions even at low current densities. The throwing power of Zn-Ni alloy was better in a solution containing ethylenediamine than triethanolamine.

UR - http://www.scopus.com/inward/record.url?scp=84878953783&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84878953783&partnerID=8YFLogxK

U2 - 10.2355/tetsutohagane.99.425

DO - 10.2355/tetsutohagane.99.425

M3 - Article

VL - 99

SP - 35

EP - 41

JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan

SN - 0021-1575

IS - 6

ER -