Electron microscopy study of preferential variant selection in copt alloy ordered under a magnetic field

Hiroshi Akamine, Sahar Farjami, Masatoshi Mitsuhara, Minoru Nishida, Takashi Fukuda, Tomoyuki Kakeshita

研究成果: ジャーナルへの寄稿記事

3 引用 (Scopus)

抄録

Transmission electron microscope (TEM) and scanning transmission electron microscope (STEM) observations were carried out to investigate microstructure formation and variant selection process in L10-type ordered CoPt alloy upon a two-step ordering heat-treatment. The first step corresponds to nucleation process carried out under a magnetic field of 10 T and the second step represents growth process without magnetic field. After the first step of ordering, ordered domains of about 5 nm in size were observed and fraction of the preferred variant with the c-axis parallel to applied magnetic field was slightly higher than that of the other two variants. Formation of tweed microstructure along {011}L10 was confirmed at the initial stage of ordering. This structure is considered to be derived from the periodic alignment of interface between two ordered variants with twin relation. At the early stage of the second step of ordering, numerous micro-twins were formed through tweed microstructure and the volume fraction of the preferred variant was increased accompanying with modulation of twins, while that of other two variants was decreased. After the second step of ordering, the twins were vanished and single variant was obtained.

元の言語英語
ページ(範囲)1715-1718
ページ数4
ジャーナルMaterials Transactions
54
発行部数9
DOI
出版物ステータス出版済み - 9 4 2013

Fingerprint

Electron microscopy
electron microscopy
Magnetic fields
Microstructure
Electron microscopes
magnetic fields
microstructure
Volume fraction
Nucleation
electron microscopes
Heat treatment
Modulation
Scanning
heat treatment
alignment
nucleation
modulation
scanning

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Electron microscopy study of preferential variant selection in copt alloy ordered under a magnetic field. / Akamine, Hiroshi; Farjami, Sahar; Mitsuhara, Masatoshi; Nishida, Minoru; Fukuda, Takashi; Kakeshita, Tomoyuki.

:: Materials Transactions, 巻 54, 番号 9, 04.09.2013, p. 1715-1718.

研究成果: ジャーナルへの寄稿記事

@article{66ec8f9a151d4fc6af2b8aff611edb94,
title = "Electron microscopy study of preferential variant selection in copt alloy ordered under a magnetic field",
abstract = "Transmission electron microscope (TEM) and scanning transmission electron microscope (STEM) observations were carried out to investigate microstructure formation and variant selection process in L10-type ordered CoPt alloy upon a two-step ordering heat-treatment. The first step corresponds to nucleation process carried out under a magnetic field of 10 T and the second step represents growth process without magnetic field. After the first step of ordering, ordered domains of about 5 nm in size were observed and fraction of the preferred variant with the c-axis parallel to applied magnetic field was slightly higher than that of the other two variants. Formation of tweed microstructure along {011}L10 was confirmed at the initial stage of ordering. This structure is considered to be derived from the periodic alignment of interface between two ordered variants with twin relation. At the early stage of the second step of ordering, numerous micro-twins were formed through tweed microstructure and the volume fraction of the preferred variant was increased accompanying with modulation of twins, while that of other two variants was decreased. After the second step of ordering, the twins were vanished and single variant was obtained.",
author = "Hiroshi Akamine and Sahar Farjami and Masatoshi Mitsuhara and Minoru Nishida and Takashi Fukuda and Tomoyuki Kakeshita",
year = "2013",
month = "9",
day = "4",
doi = "10.2320/matertrans.MAW201313",
language = "English",
volume = "54",
pages = "1715--1718",
journal = "Materials Transactions",
issn = "0916-1821",
publisher = "The Japan Institute of Metals and Materials",
number = "9",

}

TY - JOUR

T1 - Electron microscopy study of preferential variant selection in copt alloy ordered under a magnetic field

AU - Akamine, Hiroshi

AU - Farjami, Sahar

AU - Mitsuhara, Masatoshi

AU - Nishida, Minoru

AU - Fukuda, Takashi

AU - Kakeshita, Tomoyuki

PY - 2013/9/4

Y1 - 2013/9/4

N2 - Transmission electron microscope (TEM) and scanning transmission electron microscope (STEM) observations were carried out to investigate microstructure formation and variant selection process in L10-type ordered CoPt alloy upon a two-step ordering heat-treatment. The first step corresponds to nucleation process carried out under a magnetic field of 10 T and the second step represents growth process without magnetic field. After the first step of ordering, ordered domains of about 5 nm in size were observed and fraction of the preferred variant with the c-axis parallel to applied magnetic field was slightly higher than that of the other two variants. Formation of tweed microstructure along {011}L10 was confirmed at the initial stage of ordering. This structure is considered to be derived from the periodic alignment of interface between two ordered variants with twin relation. At the early stage of the second step of ordering, numerous micro-twins were formed through tweed microstructure and the volume fraction of the preferred variant was increased accompanying with modulation of twins, while that of other two variants was decreased. After the second step of ordering, the twins were vanished and single variant was obtained.

AB - Transmission electron microscope (TEM) and scanning transmission electron microscope (STEM) observations were carried out to investigate microstructure formation and variant selection process in L10-type ordered CoPt alloy upon a two-step ordering heat-treatment. The first step corresponds to nucleation process carried out under a magnetic field of 10 T and the second step represents growth process without magnetic field. After the first step of ordering, ordered domains of about 5 nm in size were observed and fraction of the preferred variant with the c-axis parallel to applied magnetic field was slightly higher than that of the other two variants. Formation of tweed microstructure along {011}L10 was confirmed at the initial stage of ordering. This structure is considered to be derived from the periodic alignment of interface between two ordered variants with twin relation. At the early stage of the second step of ordering, numerous micro-twins were formed through tweed microstructure and the volume fraction of the preferred variant was increased accompanying with modulation of twins, while that of other two variants was decreased. After the second step of ordering, the twins were vanished and single variant was obtained.

UR - http://www.scopus.com/inward/record.url?scp=84883257251&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84883257251&partnerID=8YFLogxK

U2 - 10.2320/matertrans.MAW201313

DO - 10.2320/matertrans.MAW201313

M3 - Article

AN - SCOPUS:84883257251

VL - 54

SP - 1715

EP - 1718

JO - Materials Transactions

JF - Materials Transactions

SN - 0916-1821

IS - 9

ER -