Elemental distribution near the grain boundary in a NdFeB sintered magnet subjected to grain-boundary diffusion with Dy2O3

M. Itakura, M. Namura, M. Nishida, H. Nakamura

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

We have investigated the microstructure in a NdFeB sintered magnet subjected to the grain-boundary diffusion (GBD) process with Dy2O3. It was found that thin (Nd,Dy)2Fe14B shells with a thickness of at least 10nm and an average Dy concentration of approximately 0.7 at% were formed even at the center of the specimen, at a depth of approximately 1mm from the specimen surface. However, the area fraction of the fcc NdO phase remained almost constant at approximately 3% throughout the magnet irrespective of depth, and the grain-boundary wetting phase hardly changed except in the vicinity of the surface. Furthermore, the thickness (ca. 3 nm) and structure (amorphous) of the thin grain boundary phase existing between Nd2Fe14B grains remained almost unchanged by the Dy-GBD process, despite the formation of the coreshell structure. Therefore, the Dy concentration in the thin Dy-substituted shell is important for improving the coercivity via the GBD process.

本文言語英語
ページ(範囲)438-443
ページ数6
ジャーナルMaterials Transactions
61
3
DOI
出版ステータス出版済み - 2020

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Elemental distribution near the grain boundary in a NdFeB sintered magnet subjected to grain-boundary diffusion with Dy<sub>2</sub>O<sub>3</sub>」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル