Enhancement of thermoelectric efficiency in type-VIII clathrate Ba 8Ga16Sn30 by Al substitution for Ga

Shukang Deng, Yuta Saiga, Koichiro Suekuni, Toshiro Takabatake

研究成果: ジャーナルへの寄稿記事

41 引用 (Scopus)


Single-crystalline samples of type-VIII clathrate Ba8Ga 16-xAlxSn30 (0≤x≤12) were grown from Sn flux to characterize the structural and thermoelectric properties from 300 to 600 K. The lattice parameter increases by 0.5% as x is increased to 10.5 whose value is the solubility limit of Al. The Seebeck coefficients of all samples are largely negative and the absolute values increase to approximately 300 μV/K on heating to 600 K. This large thermopower coexists with the metallic behavior in the electrical resistivity. The values of resistivity for 1≤x≤6 at 300 K are in the range 3.3-3.8 mωcm which is 70% of that for x=0. As a result, the power factor for x=4 and 6 has a rather large maximum of 1.83× 10-3 W/m K2 at 480 K. The thermal conductivity stays at a low level of 0.72 W/mK up to 480 K, and the sample with x=6 reaches a ZT value of 1.2 at 500 K.

ジャーナルJournal of Applied Physics
出版物ステータス出版済み - 10 1 2010


All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)