Epitaxial growth of ZnInON films with tunable band gap from 1.7 to 3.3 eV on ZnO templates

Koichi Matsushima, Tadafumi Hirose, Kazunari Kuwahara, Daisuke Yamashita, Giichiro Uchida, Hyunwoong Seo, Kunihiro Kamataki, Kazunori Koga, Masaharu Shiratani, Naho Itagaki

研究成果: Contribution to journalArticle

12 引用 (Scopus)

抜粋

Epitaxial ZnInON (ZION) films with a tunable band gap have been successfully fabricated by RF magnetron sputtering on ZnO templates prepared via nitrogen mediated crystallization (NMC). X-ray diffraction (XRD) measurements show that the full widths at half maximum of the rocking curves from (002) and (101) planes are small at 0.10 and 0.08°, respectively, indicating a high crystallinity with good in-plane and out-of-plane alignments. Since the coherent growth of 35-nm-thick ZION films on NMC-ZnO templates is deduced from the reciprocal space mapping around the (105) diffraction, there is little lattice relaxation at the interface between the films and templates, which is significant in terms of the suppression of carrier recombination. The band gap of the ZION films has been tuned in a wide range of 1.7-3.3 eV by changing the Zn:In ratio. These results indicate that ZION is a potential absorption layer material of solar cells.

元の言語英語
記事番号11NM06
ジャーナルJapanese journal of applied physics
52
発行部数11 PART 2
DOI
出版物ステータス出版済み - 11 1 2013

All Science Journal Classification (ASJC) codes

  • Engineering(all)
  • Physics and Astronomy(all)

フィンガープリント Epitaxial growth of ZnInON films with tunable band gap from 1.7 to 3.3 eV on ZnO templates' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用