Evolution of Ω phase in an Al-Cu-Mg-Ag alloy -a three-dimensional atom probe study

L. Reich, M. Murayama, K. Hono

研究成果: ジャーナルへの寄稿記事

220 引用 (Scopus)

抜粋

Evolution of plate-like precipitates of the Ω phase in an Al-1.9Cu-0.3Mg-0.2Ag (at.%) alloy has been investigated by three-dimensional atom probe (3DAP) and transmission electron microscope (TEM) techniques. In an as-quenched alloy, all solute atoms are uniformly dissolved. After 5 s aging at 180°C, co-clusters of Ag and Mg atoms are present. Initially, these co-clusters do not have well-defined shape, but after aging for 120 s, they are aligned on the {111} planes incorporating Cu atoms. Initially, they do not have the distinct structure consistent with the Ω phase, thus these are designated as {111}GP zones. The Ω platelet which appears after the {111}GP zones contain all solute elements within the precipitate having a composition of approximately 25 at.% Cu, 20 at.% Mg and 10 at.% Ag. In the well-defined Ω phase which appears after 2 and 10 h aging at 180°C, Ag and Mg atoms are strongly segregated to the broad face monolayer interfaces of α/Ω. No Mg and Ag are incorporated within the platelet, and its chemical composition is Al-33 at.% Cu. Based on these observations, it is concluded that the Ω phase evolves from co-clusters to plate-like precipitates continuously, rather than precipitating discretely by heterogeneous nucleation to their precursors. In a well-grown Ω plate, elemental mapping near a ledge was observed by 3DAP for the first time.

元の言語英語
ページ(範囲)6053-6062
ページ数10
ジャーナルActa Materialia
46
発行部数17
DOI
出版物ステータス出版済み - 11 1998
外部発表Yes

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

これを引用