Fabrication and evaluation of carbonate apatite-coated calcium carbonate bone substitutes for bone tissue engineering

Masako Fujioka-Kobayashi, Kanji Tsuru, Hirokazu Nagai, Kenji Fujisawa, Takaharu Kudoh, Go Ohe, Kunio Ishikawa, Youji Miyamoto

研究成果: Contribution to journalArticle査読

4 被引用数 (Scopus)

抄録

Carbonate apatite-coated calcium carbonate (CO3Ap/CaCO3) was fabricated through a dissolution–precipitation reaction using CaCO3 granules as a precursor to accelerate bone replacement based on superior osteoconductivity of the CO3Ap shell, along with Ca2+ release from the CaCO3 core and quicker resorption of the CaCO3 core. In the present study, CaCO3, 10% CO3Ap/CaCO3, 30% CO3Ap/CaCO3, and CO3Ap granules were fabricated and examined histologically to evaluate their potential as bone substitutes. Larger contents of CaCO3 in the granules resulted in higher Ca2+ release and promoted cell proliferation of murine preosteoblasts at 6 days compared with CO3Ap. Interestingly, in a rabbit femur defect model, 10% CO3Ap/CaCO3 induced significantly higher new bone formation and higher material resorption compared with CO3Ap at 8 weeks. Nevertheless, CO3Ap showed a superior osteoconductive potential compared with 10% CO3Ap/CaCO3 at 8 weeks. All tested granules were most likely resorbed by cell mediation including multinucleated giant cell functions. Therefore, we conclude that CO3Ap/CaCO3 has a positive potential for bone tissue engineering based on well-controlled calcium release, bone formation, and material resorption.

本文言語英語
ページ(範囲)2077-2087
ページ数11
ジャーナルJournal of Tissue Engineering and Regenerative Medicine
12
10
DOI
出版ステータス出版済み - 10 2018

All Science Journal Classification (ASJC) codes

  • Medicine (miscellaneous)
  • Biomaterials
  • Biomedical Engineering

フィンガープリント 「Fabrication and evaluation of carbonate apatite-coated calcium carbonate bone substitutes for bone tissue engineering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル