Fabrication and performances of all solid-state symmetric sodium battery based on NASICON-related compounds

Yoshinori Noguchi, Eiji Kobayashi, Larisa S. Plashnitsa, Shigeto Okada, Jun Ichi Yamaki

研究成果: ジャーナルへの寄稿記事

119 引用 (Scopus)

抜粋

The electrochemical performance of a novel all solid-state sodium-ion symmetrical battery with Na3Zr2Si2PO 12 (NASICON) as a solid electrolyte and Na3V 2(PO4)3 (NVP) as the active electrode material was examined. The all solid-state cell was fabricated by a combination of screen printing and hot pressing. The electrochemical characterization of the NVP active material in the metallic sodium half-cells at 80 °C indicated that this NASICON-related phosphate undergoes reversible sodium extraction/insertion reactions at electrode potentials of 1.6 and 3.4 V vs. Na. These insertion properties allowed the NVP to function successfully as the active material for both the positive and negative electrodes in a sodium-ion cell configuration. A charge-discharge cycling test of the fabricated symmetrical all solid-state cell was carried out at room temperature within the voltage range of 0.01 and 1.9 V. It was found that the cell can work as a secondary battery and showed first discharge capacities of 68 and 32 mAh g-1 at the current densities of 1.2 and 10 μA cm-2, respectively. Furthermore, the lack of reactivity between the all-solid-state cell components during long-term cycling was confirmed.

元の言語英語
ページ(範囲)59-65
ページ数7
ジャーナルElectrochimica Acta
101
DOI
出版物ステータス出版済み - 1 1 2013

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Electrochemistry

これを引用