Fabrication and properties of nonreducible lead-free piezoelectric Mn-doped (Ba,Ca)TiO3 ceramics

Wataru Sakamoto, Kouta Noritake, Hiroki Ichikawa, Koichiro Hayashi, Toshinobu Yogo

研究成果: ジャーナルへの寄稿記事

4 引用 (Scopus)

抄録

Nonreducible lead-free (Ba,Ca)TiO3 piezoceramics were fabricated by controlling the level of Mn doping. Similar to Mn-doped (Ba0.85Ca0.15)TiO3 ceramics sintered in air, stable dielectric properties with temperature change were achieved for the nonreducible sample by stabilizing the tetragonal phase of BaTiO3 over a wide temperature range. In addition, optimization of the level of Mn doping was very effective in improving the sintered density and electrical resistivity for (Ba0.85Ca0.15)TiO3 ceramics sintered under a low oxygen partial pressure. The valence state of doped Mn in nonreducible (Ba,Ca)TiO3 after sintering was confirmed to be Mn2+ or Mn3+ by electron spin resonance analysis. Sintered bodies of 1 mol% Ba excess and 1 mol% Mn-doped (Ba0.85Ca0.15)TiO3, which were sintered at 1350 °C in a H2(0.3%)/Ar atmosphere, exhibited sufficient sintered density and resistivity to allow the characterization of several electrical properties. The ferroelectric, field-induced strain, and piezoelectric properties of the nonreducible (Ba0.85Ca0.15)TiO3 ceramics sintered in the reducing atmosphere were comparable with those of (Ba0.85Ca0.15)TiO3 samples sintered in air.

元の言語英語
ページ(範囲)S166-S171
ジャーナルCeramics International
43
DOI
出版物ステータス出版済み - 8 1 2017
外部発表Yes

Fingerprint

Lead
Doping (additives)
Fabrication
Air
Partial pressure
Dielectric properties
Ferroelectric materials
Paramagnetic resonance
Electric properties
Sintering
Oxygen
Temperature

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Process Chemistry and Technology
  • Surfaces, Coatings and Films
  • Materials Chemistry

これを引用

Fabrication and properties of nonreducible lead-free piezoelectric Mn-doped (Ba,Ca)TiO3 ceramics. / Sakamoto, Wataru; Noritake, Kouta; Ichikawa, Hiroki; Hayashi, Koichiro; Yogo, Toshinobu.

:: Ceramics International, 巻 43, 01.08.2017, p. S166-S171.

研究成果: ジャーナルへの寄稿記事

Sakamoto, Wataru ; Noritake, Kouta ; Ichikawa, Hiroki ; Hayashi, Koichiro ; Yogo, Toshinobu. / Fabrication and properties of nonreducible lead-free piezoelectric Mn-doped (Ba,Ca)TiO3 ceramics. :: Ceramics International. 2017 ; 巻 43. pp. S166-S171.
@article{a91c73c7fabc4a1e8ea9c0b60ca5d959,
title = "Fabrication and properties of nonreducible lead-free piezoelectric Mn-doped (Ba,Ca)TiO3 ceramics",
abstract = "Nonreducible lead-free (Ba,Ca)TiO3 piezoceramics were fabricated by controlling the level of Mn doping. Similar to Mn-doped (Ba0.85Ca0.15)TiO3 ceramics sintered in air, stable dielectric properties with temperature change were achieved for the nonreducible sample by stabilizing the tetragonal phase of BaTiO3 over a wide temperature range. In addition, optimization of the level of Mn doping was very effective in improving the sintered density and electrical resistivity for (Ba0.85Ca0.15)TiO3 ceramics sintered under a low oxygen partial pressure. The valence state of doped Mn in nonreducible (Ba,Ca)TiO3 after sintering was confirmed to be Mn2+ or Mn3+ by electron spin resonance analysis. Sintered bodies of 1 mol{\%} Ba excess and 1 mol{\%} Mn-doped (Ba0.85Ca0.15)TiO3, which were sintered at 1350 °C in a H2(0.3{\%})/Ar atmosphere, exhibited sufficient sintered density and resistivity to allow the characterization of several electrical properties. The ferroelectric, field-induced strain, and piezoelectric properties of the nonreducible (Ba0.85Ca0.15)TiO3 ceramics sintered in the reducing atmosphere were comparable with those of (Ba0.85Ca0.15)TiO3 samples sintered in air.",
author = "Wataru Sakamoto and Kouta Noritake and Hiroki Ichikawa and Koichiro Hayashi and Toshinobu Yogo",
year = "2017",
month = "8",
day = "1",
doi = "10.1016/j.ceramint.2017.05.291",
language = "English",
volume = "43",
pages = "S166--S171",
journal = "Ceramics International",
issn = "0272-8842",
publisher = "Elsevier Limited",

}

TY - JOUR

T1 - Fabrication and properties of nonreducible lead-free piezoelectric Mn-doped (Ba,Ca)TiO3 ceramics

AU - Sakamoto, Wataru

AU - Noritake, Kouta

AU - Ichikawa, Hiroki

AU - Hayashi, Koichiro

AU - Yogo, Toshinobu

PY - 2017/8/1

Y1 - 2017/8/1

N2 - Nonreducible lead-free (Ba,Ca)TiO3 piezoceramics were fabricated by controlling the level of Mn doping. Similar to Mn-doped (Ba0.85Ca0.15)TiO3 ceramics sintered in air, stable dielectric properties with temperature change were achieved for the nonreducible sample by stabilizing the tetragonal phase of BaTiO3 over a wide temperature range. In addition, optimization of the level of Mn doping was very effective in improving the sintered density and electrical resistivity for (Ba0.85Ca0.15)TiO3 ceramics sintered under a low oxygen partial pressure. The valence state of doped Mn in nonreducible (Ba,Ca)TiO3 after sintering was confirmed to be Mn2+ or Mn3+ by electron spin resonance analysis. Sintered bodies of 1 mol% Ba excess and 1 mol% Mn-doped (Ba0.85Ca0.15)TiO3, which were sintered at 1350 °C in a H2(0.3%)/Ar atmosphere, exhibited sufficient sintered density and resistivity to allow the characterization of several electrical properties. The ferroelectric, field-induced strain, and piezoelectric properties of the nonreducible (Ba0.85Ca0.15)TiO3 ceramics sintered in the reducing atmosphere were comparable with those of (Ba0.85Ca0.15)TiO3 samples sintered in air.

AB - Nonreducible lead-free (Ba,Ca)TiO3 piezoceramics were fabricated by controlling the level of Mn doping. Similar to Mn-doped (Ba0.85Ca0.15)TiO3 ceramics sintered in air, stable dielectric properties with temperature change were achieved for the nonreducible sample by stabilizing the tetragonal phase of BaTiO3 over a wide temperature range. In addition, optimization of the level of Mn doping was very effective in improving the sintered density and electrical resistivity for (Ba0.85Ca0.15)TiO3 ceramics sintered under a low oxygen partial pressure. The valence state of doped Mn in nonreducible (Ba,Ca)TiO3 after sintering was confirmed to be Mn2+ or Mn3+ by electron spin resonance analysis. Sintered bodies of 1 mol% Ba excess and 1 mol% Mn-doped (Ba0.85Ca0.15)TiO3, which were sintered at 1350 °C in a H2(0.3%)/Ar atmosphere, exhibited sufficient sintered density and resistivity to allow the characterization of several electrical properties. The ferroelectric, field-induced strain, and piezoelectric properties of the nonreducible (Ba0.85Ca0.15)TiO3 ceramics sintered in the reducing atmosphere were comparable with those of (Ba0.85Ca0.15)TiO3 samples sintered in air.

UR - http://www.scopus.com/inward/record.url?scp=85019729454&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85019729454&partnerID=8YFLogxK

U2 - 10.1016/j.ceramint.2017.05.291

DO - 10.1016/j.ceramint.2017.05.291

M3 - Article

AN - SCOPUS:85019729454

VL - 43

SP - S166-S171

JO - Ceramics International

JF - Ceramics International

SN - 0272-8842

ER -