Fabrication and some mechanical properties of SiC whisker-reinforced Si3N4 composites utilizing underwater-shock pressure

Ryuichi Tomoshige, Akira Chiba, Minoru Nishida, Kihachiro Imamura, Shigeru Itoh, Masahiro Fujita

研究成果: Contribution to journalArticle査読

抄録

SiC whisker-reinforced Si3N4-based composites without additives were compacted by underwater-shock wave. The composites contained 10, 20 and 30 vol%SiC whisker as reinforcements. There were no macrocracks in all shock compacted composites. The as-compacted and specimens sintered at various temperatures for 5 h were characterized by the measurements of relative density, micro Vickers hardness and fracture toughness. The relative density of sintered Si3N4-10 vol%SiC whisker composite was higher than that of sintered Si3N4-20 and 30 vol%SiC whisker composites, and reached the theoretical density by sintering at 1973 K. Hardness of each composite increased up to 1823 K in proportion to sintering temperature, and then saturated above 1823 K. The hardness and fracture toughness of the Si3N4-30 vol%SiC whisker composite sintered at 1973 K were about 29 GPa and 5.0 MPa√m, respectively. The fracture toughness was 25% higher than those of monolithic Si3N4 and other obtained composites sintered at the same temperature. SEM observation showed that whisker bridging and deflection were observed in sintered composites and that the matrix of the Si3N4-30 vol%SiC whisker composite consists of plate-like and submicron order fine needle-like β-Si3N4 grains.

本文言語英語
ページ(範囲)434-440
ページ数7
ジャーナルJournal of the Ceramic Society of Japan. International ed.
101
4
出版ステータス出版済み - 4 1 1993
外部発表はい

All Science Journal Classification (ASJC) codes

  • Engineering(all)

フィンガープリント 「Fabrication and some mechanical properties of SiC whisker-reinforced Si<sub>3</sub>N<sub>4</sub> composites utilizing underwater-shock pressure」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル