Fabrication of carbonate apatite block based on internal dissolutionprecipitation reaction of dicalcium phosphate and calcium carbonate

Fumikazu Daitou, Michito Maruta, Giichiro Kawachi, Kanji Tsuru, Shigeki Matsuya, Yoshihiro Terada, Kunio Ishikawa

研究成果: Contribution to journalArticle査読

23 被引用数 (Scopus)

抄録

In this study, we investigated a novel method for fabrication of carbonate apatite block without ionic movement between precursor and solution by using precursor that includes all constituent ions of carbonate apatite. A powder mixture prepared from dicalcium phosphate anhydrous and calcite at appropriate Ca/P ratios (1.5, 1.67, and 1.8) was used as starting material. For preparation of specimens, the slurry made from the powder mixture and distilled water was packed in a split stainless steel mold and heat-treated, ranging from 60°C to 100°C up to 48 hours at 100% humidity. It appeared that carbonate apatite could be obtained above 70°C and monophasic carbonate apatite could be obtained from the powder mixture at Ca/P ratio of 1.67. Carbonate content of the specimen was about 5-7%. Diametral tensile strength of the carbonate apatite blocks slightly decreased with increasing treatment temperature. The decrease in diametral tensile strength is thought to be related to the crystal size of the carbonate apatite formed.

本文言語英語
ページ(範囲)303-308
ページ数6
ジャーナルdental materials journal
29
3
DOI
出版ステータス出版済み - 2010

All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 歯科学(全般)

フィンガープリント

「Fabrication of carbonate apatite block based on internal dissolutionprecipitation reaction of dicalcium phosphate and calcium carbonate」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル