Fabrication of deep-sub-millimeter-thick compacts using spark plasma sintering

T. Tanaka, T. Ohashi, K. Oshiro, H. Fujimori, H. Kurisu, M. Matsuura, S. Yamamoto

研究成果: 書籍/レポート タイプへの寄稿会議への寄与

抄録

Nd-Fe-B type powder was sintered using spark plasma sintering method. Fabricated compact sintered at the temperature of 700°C, is found to be a composite magnet with Nd-Fe-Co-B and α-Fe. The compact sintered at 700°C shows slightly low coercivity and large remanent magnetization comparing to the compact sintered at 600°C due to the formation of α-Fe phase, resulting in the large maximum energy product. Maximum energy product tends to decrease with decreasing thickness of sintered compacts below 0.5 mm in thickness.

本文言語英語
ホスト出版物のタイトルProgress in Powder Metallurgy - Proceedings of the 2006 Powder Metallurgy World Congress and Exhibition (PM 2006)
出版社Trans Tech Publications Ltd
ページ521-524
ページ数4
PART 1
ISBN(印刷版)0878494197, 9780878494194
DOI
出版ステータス出版済み - 2007
外部発表はい
イベント2006 Powder Metallurgy World Congress and Exhibition, PM 2006 - Busan, 韓国
継続期間: 9月 24 20069月 28 2006

出版物シリーズ

名前Materials Science Forum
番号PART 1
534-536
ISSN(印刷版)0255-5476
ISSN(電子版)1662-9752

その他

その他2006 Powder Metallurgy World Congress and Exhibition, PM 2006
国/地域韓国
CityBusan
Period9/24/069/28/06

!!!All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Fabrication of deep-sub-millimeter-thick compacts using spark plasma sintering」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル