Fabrication of poly(p-phenylenebenzobisoxazole) film using a soluble poly(o -alkoxyphenylamide) as the precursor

Takahiro Fukumaru, Yusuke Saegusa, Tsuyohiko Fujigaya, Naotoshi Nakashima

    研究成果: ジャーナルへの寄稿学術誌査読

    23 被引用数 (Scopus)


    Poly(p-phenylenebenzobisoxazole) (PPBO) is a polymer having the most excellent thermal properties among the organic polymers reported to date, and the design and the preparation of PPBO with the desired shape and form are expected to provide novel PPBO-based devices and materials in the fields of automobiles, aerospace, microelectronics, etc. We here describe the fabrication and characterization of PPBO films via the solution-casting and successive thermal conversion of its precursor, alkyl-substituted hydroxypolyamides (poly(o-alkoxyphenylamide)s) that were synthesized by a low-temperature polycondensation reaction of dialkoxydiaminobenzene with terephthaloyl chloride in N-methylpyrrolidone. The formation mechanism of the thermal conversion was carefully investigated based on the analyses of the results using TGA, IR, pyrolysis gas chromatography mass spectrometry (Py-GC/MS), and evolved gas analysis GC/MS (EGA-GC/MS) measurements. A transparent PPBO precursor film provided a PPBO film after thermal treatment at 250 °C for 6 h and then at 300 °C for 6 h under vacuum. The obtained PPBO film showed excellent mechanical properties (tensile strength = 76 MPa, Young's modulus = 2.7 GPa) as well as a high thermal stability (temperature of 5 wt % loss = 670 °C). Such outstanding mechanical and thermal properties would significantly contribute to fulfill the requirements for next generation extreme materials/devices.

    出版ステータス出版済み - 3月 25 2014

    !!!All Science Journal Classification (ASJC) codes

    • 有機化学
    • ポリマーおよびプラスチック
    • 無機化学
    • 材料化学


    「Fabrication of poly(p-phenylenebenzobisoxazole) film using a soluble poly(o -alkoxyphenylamide) as the precursor」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。