Failure damage evolution of a mechanical joint of carbon fiber metal laminates under the bearing failure mode

Terutake Matsubara, Yoshihiro Takao, Wen Xue Wang

研究成果: Chapter in Book/Report/Conference proceedingConference contribution

抄録

Glass fiber-reinforced metal laminates have already been developed as Glare and used in A380 as upper fuselage panels. Though a lot of efforts were made to develop Carbon Fiber-reinforced Metal Laminates (CFMLs), two major problems were unsolved. They were the galvanic corrosion and large thermal residual stresses. A new galvanic corrosion-resistant coating has successfully proposed, which consists of a sulfuric acid anodizing and a silica nano-particle reinforced hybrid sol-gel coating. This paper investigates the damage evolution of a mechanical pin joint of CFML with the new coating under the quasi-static tensile loading. Two peaks of load and their damage evolutions are identified by the microscopic fracture analysis.

本文言語英語
ホスト出版物のタイトルProgress of Composites 2008 in Asia and Australasia - Proceedings of the 6th Asian-Australasian Conference on Composite Materials, ACCM 2008
ページ188-191
ページ数4
出版ステータス出版済み - 12 1 2008
イベント6th Asian-Australasian Conference on Composite Materials: Progress of Composites 2008 in Asia and Australasia, ACCM 2008 - Kumamoto, Kyushu, 日本
継続期間: 9 23 20089 26 2008

出版物シリーズ

名前Progress of Composites 2008 in Asia and Australasia - Proceedings of the 6th Asian-Australasian Conference on Composite Materials, ACCM 2008

その他

その他6th Asian-Australasian Conference on Composite Materials: Progress of Composites 2008 in Asia and Australasia, ACCM 2008
国/地域日本
CityKumamoto, Kyushu
Period9/23/089/26/08

All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料

フィンガープリント

「Failure damage evolution of a mechanical joint of carbon fiber metal laminates under the bearing failure mode」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル