Fatigue and fracture behaviour of structural Al-alloys up to very long life regimes

Q. Y. Wang, N. Kawagoishi, Q. Chen

研究成果: Contribution to journalArticle査読

64 被引用数 (Scopus)

抄録

Very long life fatigue and near-threshold fatigue crack growth behaviour of 7075 and 6061 Al-alloys in T6 condition were investigated using accelerated fatigue testing at 19.5 kHz on a piezoelectric machine. Significant interfacial voids were observed in the two Al-alloys during crack initiation and early fatigue crack growth process. Fatigue failure in Al-alloys could be ascribed to: the formation of a number of fatigue voids, their growth and coalescence, and the subsequent formation and propagation of macroscopic cracks. Moreover, fatigue crack growth rates of small cracks in these alloys were found to be greater than those of large cracks for the same stress intensity factor range.

本文言語英語
ページ(範囲)1572-1576
ページ数5
ジャーナルInternational Journal of Fatigue
28
11
DOI
出版ステータス出版済み - 11 2006
外部発表はい

All Science Journal Classification (ASJC) codes

  • Modelling and Simulation
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

フィンガープリント 「Fatigue and fracture behaviour of structural Al-alloys up to very long life regimes」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル