Fatigue properties of inconel 718 in long life region at elevated temperature

N. Yan, N. Kawagoishi, Q. Chen, Q. Y. Wang, H. Nisitani, E. Kondo

研究成果: Contribution to journalConference article

14 被引用数 (Scopus)

抄録

The fatigue properties of Inconel 718 in long life region up to 108 cycles were investigated under rotating bending at room temperature and 500°C. The early propagation of a crack was suppressed by oxide induced crack closure. Consequently, fatigue strength was higher at 500°C than at room temperature. Surface fracture occurred at high stress levels and internal fracture occurred in long life region beyond 107 cycles at 500°C. Correspondingly, S-N curve at 500°C presented in a step-wise shape, compared to the conventional one-step shape at room temperature. Intergranular cracking was observed at the origins of internal fracture at 500°C.

本文言語英語
ページ(範囲)321-326
ページ数6
ジャーナルKey Engineering Materials
243-244
DOI
出版ステータス出版済み - 1 1 2003
外部発表はい
イベントProceedings of the International Conference on Experimental and Computational Mechanics in Engineering - Dunhuang, 中国
継続期間: 8 24 20028 27 2002

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Fatigue properties of inconel 718 in long life region at elevated temperature」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル