Fatigue properties of Ni-base superalloy in long life region at elevated temperature

Norio Kawagoishi, Qiang Chen, Ken Ichi Otsubo, Nu Yan, Eiji Kondo, Qingyuan Wang

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

The fatigue properties of a nickel-base superalloy, Inconel 718, in long-life region up to 108 cycles were investigated under rotating bending at room temperature and elevated temperature of 300°C, 500°C and 600°C. S-N curves at 500°C and 600°C showed the stepwise shapes, though those in cases of room temperature and 300°C were the conventional one-step ones. All the fractures originated from the specimen surface at room temperature and 300°C, while the internal fractures occurred in long-life region beyond 107 cycles and the surface fractures at the stress levels over the horizontal line of S-N curves corresponding to the fatigue limit for the surface fracture at 500°C and 600°C. Intergranular cracking were observed at the origin of internal fracture.

本文言語英語
ページ(範囲)1192-1197
ページ数6
ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
68
8
DOI
出版ステータス出版済み - 8 2002
外部発表はい

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Fatigue properties of Ni-base superalloy in long life region at elevated temperature」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル