Fatigue Resistance of Laminated and Non-laminated TRIP-maraging Steels: Crack Roughness vs Tensile Strength

Zhao Zhang, Motomichi Koyama, Meimei Wang, Cemal Cem Tasan, Hiroshi Noguchi

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

Pre-cold-rolling before annealing in transformation-induced plasticity (TRIP) maraging steels changes the microstructural morphology from lamellar to granular, increasing the tensile strength. However, fatigue tests of plain specimens at ambient temperature and the stress ratio − 1 show that increased strength does not improve the fatigue strength compared to laminated TRIP-maraging steel, irrespective of stress amplitude. The disappearance of fatigue crack roughness suppresses the improvement in fatigue resistance with increasing strength.

本文言語英語
ページ(範囲)1142-1145
ページ数4
ジャーナルMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
50
3
DOI
出版ステータス出版済み - 3 15 2019

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

フィンガープリント 「Fatigue Resistance of Laminated and Non-laminated TRIP-maraging Steels: Crack Roughness vs Tensile Strength」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル