Fatigue strength characteristics evaluation of SUH660 considering small fatigue crack propagation behavior and hardness distribution

研究成果: Contribution to journalArticle査読

5 被引用数 (Scopus)

抄録

The fundamental characteristics of SUH660, which a precipitation- strengthened stainless steel, were investigated by tensile, fatigue, and Vickers hardness tests. Owing to the observed crack propagation mechanisms, the S-N diagram had two "fatigue limits": the fatigue strength at 10 7 cycles and the safe side of the fatigue limit based on the threshold of PSB crack propagation. There was significant variability between the Vickers hardness distributions of the test zones, which indicated the existence of high and low hardness zones in a single specimen. It was observed that more cracks were initiated and propagated in the low hardness zone than in the high hardness zone. Therefore, the fatigue strength of SUH660 steel is low compared to its high tensile strength.

本文言語英語
ページ(範囲)1-11
ページ数11
ジャーナルInternational Journal of Fatigue
63
DOI
出版ステータス出版済み - 6 2014

All Science Journal Classification (ASJC) codes

  • Modelling and Simulation
  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Industrial and Manufacturing Engineering

フィンガープリント 「Fatigue strength characteristics evaluation of SUH660 considering small fatigue crack propagation behavior and hardness distribution」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル