Field-effect transistors with vacuum-deposited organic-inorganic perovskite films as semiconductor channels

研究成果: Contribution to journalArticle

3 引用 (Scopus)

抜粋

Films of the organic-inorganic layered perovskite (C6H5C2H4NH3)2SnI4 were vacuum-deposited on substrates heated at various temperatures (Tsub) to investigate the influence of Tsub on their film quality and transistor performance (hole mobilities, threshold voltages, and current on/off ratios). Appropriate substrate heating at Tsub = 60 °C during vacuum deposition led to better-developed perovskite films with larger grains. These films exhibited the best transistor performance in comparison with films fabricated at the other Tsub. The transistor performance was further enhanced by reducing perovskite semiconductor thickness (t) because of a reduction of bulk resistance in a top-contact/bottom-gate transistor structure. By utilizing the optimized Tsub of 60 °C and t of 31 nm, we obtained the most improved hole mobility of 0.78 ± 0.24 cm2/V s, about 5000 times the hole mobilities of our initial transistors fabricated at Tsub = 24 °C and t = 50 nm.

元の言語英語
記事番号233301
ジャーナルJournal of Applied Physics
120
発行部数23
DOI
出版物ステータス出版済み - 12 21 2016

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

フィンガープリント Field-effect transistors with vacuum-deposited organic-inorganic perovskite films as semiconductor channels' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用