Finite element modeling of plasticity-induced crack closure due to occasional mode II loading on mode I fatigue crack growth

H. Matsunaga, M. Makizaki, K. Yanase

研究成果: Contribution to journalArticle査読

4 被引用数 (Scopus)

抄録

Plasticity-induced fatigue crack closure associated with occasional mode II loading was simulated for two-dimensional middle-crack tension geometry by using the finite element method. When a single mode II cycle was superposed onto the steady-state mode I crack growth, the range of crack tip opening displacement, δCTOD, exhibited the initial drop and subsequent recovery under plane strain condition. On the other hand, under plane stress condition, δCTOD exhibited the initial jump and drop right after the single mode II loading, and then it showed the recovery. The present results indicate that occasional mode II loading can cause a small retardation for mode I crack growth due to the enhanced plasticity-induced closure.

本文言語英語
ページ(範囲)38-49
ページ数12
ジャーナルEngineering Fracture Mechanics
111
DOI
出版ステータス出版済み - 10 2013

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Finite element modeling of plasticity-induced crack closure due to occasional mode II loading on mode I fatigue crack growth」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル