Formation and physical property of molten calcium ferrite in iron ore sinter

研究成果: 著書/レポートタイプへの貢献会議での発言

1 引用 (Scopus)

抄録

Effects of adding SiO2 or Al2O3 as additives on the viscosity and on the surface tension of calcium ferrite melts. CaO Fe2O3 (CF) and CaO 2Fe2O 3(CF2), have teen examined and the effects of SiO 2 and Al2O3 addition on the melt formation rate in calcium ferrite system were also investigated. The viscosity of calcium ferrite melts was increased, and the surface tension of calcium ferrite melts was decreased with, increase the contents of SiO2 or Al 2O3. At the same content of additive oxide, the addition of Al2O3 was more effective for increasing the viscosity than the addition of SiO2. On the contrary, the addition of SiO 2 was more effective for decreasing the surface tension than the addition of Al2O3. The effect of SiO2 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The effect of Al2O3 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The softening and melting rates of sample in CF system were also larger than that of sample in CF2 system.

元の言語英語
ホスト出版物のタイトル2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries
ページ571-577
ページ数7
1
出版物ステータス出版済み - 12 1 2004
イベント2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and Parallel Event- 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries - Victoria, espirito Santo, ブラジル
継続期間: 9 12 20049 15 2004

その他

その他2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and Parallel Event- 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries
ブラジル
Victoria, espirito Santo
期間9/12/049/15/04

Fingerprint

Iron ore sinter
Ferrite
Molten materials
Calcium
Physical properties
Surface tension
Viscosity
Melting
Oxides

All Science Journal Classification (ASJC) codes

  • Engineering(all)

これを引用

Maeda, T., Nakashima, K., & Shimizu, M. (2004). Formation and physical property of molten calcium ferrite in iron ore sinter. : 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries (巻 1, pp. 571-577)

Formation and physical property of molten calcium ferrite in iron ore sinter. / Maeda, Takayuki; Nakashima, Kunihiko; Shimizu, Masakata.

2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries. 巻 1 2004. p. 571-577.

研究成果: 著書/レポートタイプへの貢献会議での発言

Maeda, T, Nakashima, K & Shimizu, M 2004, Formation and physical property of molten calcium ferrite in iron ore sinter. : 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries. 巻. 1, pp. 571-577, 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and Parallel Event- 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries, Victoria, espirito Santo, ブラジル, 9/12/04.
Maeda T, Nakashima K, Shimizu M. Formation and physical property of molten calcium ferrite in iron ore sinter. : 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries. 巻 1. 2004. p. 571-577
Maeda, Takayuki ; Nakashima, Kunihiko ; Shimizu, Masakata. / Formation and physical property of molten calcium ferrite in iron ore sinter. 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries. 巻 1 2004. pp. 571-577
@inproceedings{7aaea10d71b74b9aa46d1adfaf7b0212,
title = "Formation and physical property of molten calcium ferrite in iron ore sinter",
abstract = "Effects of adding SiO2 or Al2O3 as additives on the viscosity and on the surface tension of calcium ferrite melts. CaO Fe2O3 (CF) and CaO 2Fe2O 3(CF2), have teen examined and the effects of SiO 2 and Al2O3 addition on the melt formation rate in calcium ferrite system were also investigated. The viscosity of calcium ferrite melts was increased, and the surface tension of calcium ferrite melts was decreased with, increase the contents of SiO2 or Al 2O3. At the same content of additive oxide, the addition of Al2O3 was more effective for increasing the viscosity than the addition of SiO2. On the contrary, the addition of SiO 2 was more effective for decreasing the surface tension than the addition of Al2O3. The effect of SiO2 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The effect of Al2O3 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The softening and melting rates of sample in CF system were also larger than that of sample in CF2 system.",
author = "Takayuki Maeda and Kunihiko Nakashima and Masakata Shimizu",
year = "2004",
month = "12",
day = "1",
language = "English",
isbn = "8586778753",
volume = "1",
pages = "571--577",
booktitle = "2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries",

}

TY - GEN

T1 - Formation and physical property of molten calcium ferrite in iron ore sinter

AU - Maeda, Takayuki

AU - Nakashima, Kunihiko

AU - Shimizu, Masakata

PY - 2004/12/1

Y1 - 2004/12/1

N2 - Effects of adding SiO2 or Al2O3 as additives on the viscosity and on the surface tension of calcium ferrite melts. CaO Fe2O3 (CF) and CaO 2Fe2O 3(CF2), have teen examined and the effects of SiO 2 and Al2O3 addition on the melt formation rate in calcium ferrite system were also investigated. The viscosity of calcium ferrite melts was increased, and the surface tension of calcium ferrite melts was decreased with, increase the contents of SiO2 or Al 2O3. At the same content of additive oxide, the addition of Al2O3 was more effective for increasing the viscosity than the addition of SiO2. On the contrary, the addition of SiO 2 was more effective for decreasing the surface tension than the addition of Al2O3. The effect of SiO2 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The effect of Al2O3 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The softening and melting rates of sample in CF system were also larger than that of sample in CF2 system.

AB - Effects of adding SiO2 or Al2O3 as additives on the viscosity and on the surface tension of calcium ferrite melts. CaO Fe2O3 (CF) and CaO 2Fe2O 3(CF2), have teen examined and the effects of SiO 2 and Al2O3 addition on the melt formation rate in calcium ferrite system were also investigated. The viscosity of calcium ferrite melts was increased, and the surface tension of calcium ferrite melts was decreased with, increase the contents of SiO2 or Al 2O3. At the same content of additive oxide, the addition of Al2O3 was more effective for increasing the viscosity than the addition of SiO2. On the contrary, the addition of SiO 2 was more effective for decreasing the surface tension than the addition of Al2O3. The effect of SiO2 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The effect of Al2O3 addition on the formation rate of molten calcium ferrite was affected that it added to CF rather than CF2. The softening and melting rates of sample in CF system were also larger than that of sample in CF2 system.

UR - http://www.scopus.com/inward/record.url?scp=33644980732&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=33644980732&partnerID=8YFLogxK

M3 - Conference contribution

SN - 8586778753

VL - 1

SP - 571

EP - 577

BT - 2nd International Meeting on Ironmaking and 1st International Symposium on Iron Ore and parallel event - 5th Japan-Brazil Symposium on Dust Processing-Energy-Environment on Metallurgical Industries

ER -