Formation of poly (2-vinylpyridine) films on Zn by galvanostatic electropolymerization

Hiroaki Nakano, Yuki Kuwahara, Satoshi Oue, Shigeo Kobayashi, Hisaaki Fukushima, Jeong Mo Yoon

    研究成果: ジャーナルへの寄稿学術誌査読

    3 被引用数 (Scopus)

    抄録

    Poly(2-vinylpyridine) films were deposited on Zn substrate by electropolymerization using galvanostatic technique at 30°C in pH 5 aqueous solution containing methanol. Films were also formed by employing cyclic voltammetry and potentiostatic techniques; these were compared with those formed using galvanostatic electrolysis. The thickness of films formed by galvanostatic electrolysis increased in proportion to the amount of charge passed during electropolymerization but decreased with increasing current density because of increased hydrogen evolution. The FT-IR spectra and the color of the films suggested that the structure of poly (2-vinylpyridine) films changed from the non-branched to the branched chain type with the higher current densities. The anodic current density for Zn dissolution in 3%NaCl solution was significantly decreased by coating with poly (2-vinylpyridine) films. After electropolymerization at 50A · m -2, the anodic reaction was most inhibited, showing excellent corrosion resistance. Although the electrochemical techniques employed for the film preparation had no influence on the thickness or the structure of films, the films formed by galvanostatic electrolysis contained the fewest cracks and gave the best corrosion resistance.

    本文言語英語
    ページ(範囲)780-786
    ページ数7
    ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
    69
    8
    DOI
    出版ステータス出版済み - 8月 1 2005

    !!!All Science Journal Classification (ASJC) codes

    • 凝縮系物理学
    • 材料力学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Formation of poly (2-vinylpyridine) films on Zn by galvanostatic electropolymerization」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル